Material Notes:
Feature: Injection Molding, Heat ResistanceApplication: Electric & Electronic Housing (Frame etc) Automotives Interior & Exterior Housing (lamp housing etc)CAS No. 25120-20-1, 9003-56-9, 25747-74-7 and 9003-54-7Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 9.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 9.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 108
108
ASTM D785
Tensile Strength, Yield 49.0 MPa

@Thickness 3.20 mm
 7110 psi

@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 25 %

@Thickness 3.20 mm
 25 %

@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 78.5 MPa

@Thickness 3.20 mm
 11400 psi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Flexural Modulus 2.55 GPa

@Thickness 3.20 mm
 370 ksi

@Thickness 0.126 in
 15 mm/min; ASTM D790
Izod Impact, Notched 2.16 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 4.04 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
2.26 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 4.22 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Izod Impact, Unnotched 0.785 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 1.47 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
0.883 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 1.65 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 105 °C

@Thickness 6.40 mm
 221 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C

@Thickness 6.40 mm
 203 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 102 °C

@Load 5.00 kg
 216 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
UL RTI, Mechanical with Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
UL RTI, Mechanical without Impact 60.0 °C

@Thickness >=1.50 mm
 140 °F

@Thickness >=0.0591 in
 UL 746B
60.0 °C

@Thickness >=3.00 mm
 140 °F

@Thickness >=0.118 in
 UL 746B
Flammability, UL94 HB

@Thickness >=1.50 mm
 HB

@Thickness >=0.0591 in
HB

@Thickness >=3.00 mm
 HB

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Strength 33.0 kV/mm

@Thickness 1.00 mm
 838 kV/in

@Thickness 0.0394 in
 ASTM D149
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Comparative Tracking Index >= 600 V
>= 600 V
Solution A; IEC 60112
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=1.50 mm
 7.0 - 15 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=3.00 mm
 15 - 30 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 25.4 - 50.0 mm/min
1.00 - 1.97 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 180 - 210 °C
356 - 410 °F
Injection Molding
Middle Barrel Temperature 210 - 230 °C
410 - 446 °F
Injection Molding
Front Barrel Temperature 230 - 240 °C
446 - 464 °F
Injection Molding
Nozzle Temperature 230 - 240 °C
446 - 464 °F
Injection Molding
Melt Temperature 220 - 240 °C
428 - 464 °F
Injection Molding
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection Molding
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 50 - 100 rpm
50 - 100 rpm
Injection Molding