SABIC Innovative Plastics LNP STAT-KON DX04490 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX04490 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* DX04490 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0042 cm/cm @Time 86400 sec |
0.0042 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ASTM D638 |
| 54.0 MPa | 7830 psi | ISO 527 | |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| 61.0 MPa | 8850 psi | ISO 527 | |
| Elongation at Break | 8.5 % | 8.5 % | ISO 527 |
| 16.3 % | 16.3 % | ASTM D638 | |
| Elongation at Yield | 4.2 % | 4.2 % | ASTM D638 |
| 4.5 % | 4.5 % | ISO 527 | |
| Tensile Modulus | 2.71 GPa | 393 ksi | 1 mm/min; ISO 527 |
| 2.98 GPa | 432 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 75.0 MPa | 10900 psi | ISO 178 |
| 89.0 MPa | 12900 psi | ASTM D790 | |
| Flexural Modulus | 2.51 GPa | 364 ksi | ISO 178 |
| 2.71 GPa | 393 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 23.42 J/cm | 43.88 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 167 kJ/m² | 79.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 4.00 J | 2.95 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 9.00 J | 6.64 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 63.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
35.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 59.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 60.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 132 °C @Thickness 3.20 mm |
270 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 100 ohm-cm - 1e+05 | 100 ohm-cm - 1e+05 | ASTM D257 |
| Surface Resistance | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 115 TC Ground Alumina
- Polymax® Maxelast® P2950 TPE, PP Overmold or Standalone use
- DSM Arnite® AV2 370 /B AV2 370 PET-35% Glass Reinforced (European and Asian Grade) (discontinued **)
- LG Chemical SEETEC BS500 LDPE
- LG Chemical Lupoy 1300-10 Polycarbonate Resin
- ExxonMobil 460 Mobilith SHC PM
Copyright © lookpolymers.com All Rights Reserved