- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 221 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 221 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 45FS PC/ABS-blend, Flame Retardant Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | 120°C/h; ISO 75/1 |
| Polykemi AB POLYblend 83FR PC/ABS-Blend, Flame Retardant, Halogen Free Information provided by Polykemi AB |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C @Thickness 3.20 mm |
221 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Lexan® BPL1000 PC (Asia Pacific) Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with U.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| PolyMirae Moplen HF524J BDDP Film Grade Polypropylene Moplen HF524J is the Addiform polypropylene. Compared to ordinary pelletized polypropylene, Addiform gives significant advantages in terms of improved productivity, better processing and lower energ.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Hyosung Topilene J640 PP J640 Injection Impact CopolymerApplications:General purposeBattery caseElectric applianceCharacteristics:Medium ImpactFlowabilityInformation provided by Hyosung Corporation |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Hyosung Topilene J640U PP J640U Injection Impact CopolymerApplications:General purposeBattery caseElectric applianceCharacteristics:Medium ImpactFlowabilityWeatherabilityInformation provided by Hyosung Corporation |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Flint Hills P9M7R-056 Specialty Homopolymer Polypropylene Clarified, e-beam and Gamma radiation sterilizable and Autoclavable. Product does not contain animal derived components. Phthalate-free.Applications: Injection molding - Lab ware, Pipette tips.In.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| LG Chemical SEETEC H7411 Polypropylene, Homopolymer Features: Seetec H7411 is designed for the extrusion of continuous filament (CF) and staple fibers. This grade is characterized by high tenacity from narrow molecular weight distribution (MWD) and U.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| LG Chemical SEETEC M1700 Polypropylene Impact Copolymer Features: SEETEC M1700 is a heterophasic polypropylene copolymer for injection molding applications. SEETEC M1700 exhibits a very high flowability and a good balance of stiffness and impact strength.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| LATI Latene® 22H2 MX/25 PP Homopolymer, Heat Stabilized Polypropylene homopolymer (PPh) based compound. Heat stabilized. Special mineral filler. Very good surface appearance.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North A.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| LATI Latigray 53/22-01 CX/25 PP Homopolymer, Impact Modified Radiopaque compound based on Polypropylene homopolymer (PPh), impact modified. Special mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformatio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics NORYL V03505 PPE+HIPS (Europe-Africa-Middle East) Noryl* V03505 is a 35% milled fiber reinforced, injection moldable grade. Designed for good dimensional stability and low warpage, this resin also uses non-chlorinated, non-brominated FR additives t.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP ML004S PP LNP* LUBRICOMP* ML004S is a compound based on Polypropylene resin containing 20% PTFE. Added features of this material include: Wear Resistant, Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75 |
| Styrolution Terblend® N NG-02 UV ABS / PA, 8% Glass filled Terblend N NG-02 UV is an 8% glass fiber reinforced (UV stabilized) ABS/PA blend with enhanced dimensional stability and rigidity.High dimensional stabilityEnhanced rigidityEnhanced softening temper.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| SCG Chemicals EL-Proâ„¢ P640J Polypropylene Injection Molding Key Characteristics:Good flowabilityHigh stiffnessHigh impact strengthRecommended Applications:High impact electrical appliance parts, automotive and motorcycle parts such as fan stand, washing tubI.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| SCG Chemicals EL-Proâ„¢ P841J Polypropylene Injection Molding Key Characteristics:Excellent flowabilityExcellent processabilityHigh stiffnessSuitable for complex parts and large partsContains UV stabilizer and anti-static agentRecommended Applications:Electric.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| A. Schulman POLYFORT™ PP 3153 Homopolymer Polypropylene DescriptionPolyfort® PP 3153 is a homopolymer polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene DescriptionPolyfort® FPP 1697HU is a high flow fortified polypropylene with high temperature dimensioned stability. It is stabilized for UV exposure and available in matched automotive color.Infor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 4529 Mineral Filled Copolymer Polypropylene DescriptionPolyfort® FPP 4528 is a mineral filled copolymer polypropylene for applications requiring good impact and increased stiffness with long term heat stability.Information provided by A. Sch.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3391 Chemically Coupled, Modified Polypropylene DescriptionPolyfort® FPP 3391 is a chemically coupled, mineral reinforced high impact resistant, modified polypropylene.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 3454F Talc Filled Copolymer DescriptionPolyfort® FPP 3454F is a 20% talc filled copolymer.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene DescriptionPolyfort® FPP 1697HU is a high flow fortified polypropylene with high temperature dimensioned stability. It is stabilized for UV exposure and available in matched automotive color.Infor.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | HDT B flatwise |
| Corbion Purac Blend A High Heat Homopolymer PLA Heat resistance higher than typical PLA is achieved by addition of a nucleating agent and PDLA homopolymer. Data is for samples produced from Puralact L and D lactide monomers; Purac also produces .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | |
| Covestro Bayblend® T 45 MN Polycarbonate/ABS Blend High impact and notched impact strength, little risk of brittle fracture, high dimensional accuracy, good platable.Information provided by Bayer.As of 1 September 2015, Bayer MaterialScience was sep.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75-1/-2 |
| EMS-Grivory Grivory® R 50 H NZ PA6 Product description: Grilon R 50 H NZ is a high viscosity, unreinforced, heat stabilized, impact modified PA6 extrusion blow molding grade. Grilon R 50 H NZ has the following important properties: V.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ISO 75-1/-2 |
| Covestro Makroblend® DP UT3905 Polycarbonate + PBT, Impact Grade Developmental product(PC+PBT)-blendhigh flowimpact modifiedeasy releaseinjection molding grade Makroblend DP UT3905* offers superior flowability, good impact strength and excellent chemical resist.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| Aclo Accutech ABS ABS834G30L Glass Reinforced |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | ASTM D648 |
| A. Schulman POLYPUR™ FPU 1156 Thermoplastic Polyurethane Information provided by A. Schulman. |
|||