Eastman Tenite 131E-28 Cellulose Acetate (discontinued **)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Tenite 131E-28 Cellulose Acetate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
28% plasticized and contains 50% fiber grade ester.ISO data as provided by the manufacturer, Eastman Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | 50 mm/min |
| Elongation at Break | 16 % | 16 % | |
| Elongation at Yield | 3.2 % | 3.2 % | |
| Tensile Modulus | 2.08 GPa | 302 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.47 J/cm² | 7.00 ft-lb/in² | |
| 0.610 J/cm² @Temperature -30.0 °C |
2.90 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 111 µm/m-°C @Temperature 20.0 °C |
61.7 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 133 µm/m-°C @Temperature 20.0 °C |
73.9 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | |
| Vicat Softening Point | 84.0 °C | 183 °F | |
| Glass Transition Temp, Tg | 99.0 °C | 210 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 240 °C | 428 - 464 °F |
Users viewing this material also viewed the following:
- LATI LASTIROL R-V2 Polystyrene (PS) (UL94 V-2) (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP D7002IXH PC
- Lubrizol ESTANE® T5384 Ether Based Thermoplastic Polyurethane (European Grade)
- Zircar Ceramics AB Alumina Blanket
- Trelleborg E715 EPDM Rubber
- Eurotec® Tecomid® NA40 NL RM PA 6.6 low friction and wear
- Azoty Tarnow™ Tarnamid® T-27 GF30 FRV0 Polyamide 6 - Flame Retarded, Reinforced
- 3M 8427-6 Cold Shrink Connector Insulators
Copyright © lookpolymers.com All Rights Reserved