Styron EMERGEâ„¢ 7700 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Styron
Trade Name EMERGE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron EMERGEâ„¢ 7700 Polycarbonate (PC) / Acrylonitrile Butadiene Styrene (ABS).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: EMERGEâ„¢ PC/ABS 7700 Advanced Resin is an ignition-resistant PC/ABS blend that contains no chlorine for bromine additives. It has superior processability for injection molding applications. This grade has excellent aesthetics, is UV stabilized and is available in custom colors. Applications:Medical equipment housingsConsumer ElectronicsInformation technology equipmentInformation provided by Styron
Physical Properties Metric English Comments
Density 1.17 g/cc
0.0423 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 11 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 11 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120

@Thickness 3.20 mm
 120

@Thickness 0.126 in
 Injection Molded; ASTM D785
Tensile Strength at Break 48.3 MPa

@Thickness 3.20 mm
 7010 psi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Tensile Strength, Yield 60.0 MPa

@Thickness 3.20 mm
 8700 psi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Elongation at Break 65 %

@Thickness 3.20 mm
 65 %

@Thickness 0.126 in
 Injection Molded; ASTM D638
Elongation at Yield 3.8 %

@Thickness 3.20 mm
 3.8 %

@Thickness 0.126 in
 Injection Molded; ASTM D638
Tensile Modulus 2.62 GPa

@Thickness 3.20 mm
 380 ksi

@Thickness 0.126 in
 Injection Molded; ASTM D638
Flexural Strength 96.5 MPa

@Thickness 3.20 mm
 14000 psi

@Thickness 0.126 in
 Injection Molded; ASTM D790
Flexural Modulus 2.69 GPa

@Thickness 3.20 mm
 390 ksi

@Thickness 0.126 in
 Injection Molded; ASTM D790
Izod Impact, Notched 2.00 J/cm

@Thickness 3.20 mm,
Temperature -18.0 °C
 3.75 ft-lb/in

@Thickness 0.126 in,
Temperature -0.400 °F
 Injection Molded; ASTM D256
5.90 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 11.1 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 Injection Molded; ASTM D256
Charpy Impact, Notched 1.20 J/cm²

@Temperature -30.0 °C
 5.71 ft-lb/in²

@Temperature -22.0 °F
 Injection Molded; ISO 179/1eA
4.50 J/cm²

@Temperature 23.0 °C
 21.4 ft-lb/in²

@Temperature 73.4 °F
 Injection Molded; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 68.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM D696
CTE, linear, Transverse to Flow 68.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 96.1 °C
205 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Unannealed; ASTM D648
Vicat Softening Point 110 °C

@Load 1.02 kg
 230 °F

@Load 2.25 lb
 Rate B (120°C/h); ASTM D1525
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
5VB

@Thickness 2.00 mm
 5VB

@Thickness 0.0787 in
Processing Properties Metric English Comments
Melt Temperature 238 - 274 °C
460 - 525 °F
Mold Temperature 60.0 - 90.6 °C
140 - 195 °F
Drying Temperature 82.2 - 87.8 °C
180 - 190 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour