- Styron EMERGEâ„¢ 5100 Acrylonitrile Butadiene Styrene (ABS)
Styron EMERGEâ„¢ 5100 Acrylonitrile Butadiene Styrene (ABS)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Styron |
| Trade Name | EMERGE™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron EMERGEâ„¢ 5100 Acrylonitrile Butadiene Styrene (ABS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
EMERGEâ„¢ ABS 5100 is a pre-colored, white, ABS resin, having high opacity and excellent toughness intended for manufacture of laser-marketable injection-molded smart cards.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4/D2 |
| Melt Flow | 8.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
8.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 28.0 MPa | 4060 psi | 100mm/min, 4mm injection molded, unannealed; ISO 527-2 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | 100mm/min, 4mm injection molded, unannealed; ISO 527-2 |
| Elongation at Break | 25 % | 25 % | 100mm/min, 4mm injection molded, unannealed; ISO 527-2 |
| Elongation at Yield | 2.5 % | 2.5 % | 100mm/min, 4mm injection molded, unannealed; ISO 527-2 |
| Tensile Modulus | 1.90 GPa | 276 ksi | 1mm/min, 4mm injection molded, unannealed; ISO 527-2 |
| Flexural Strength | 53.0 MPa @Thickness 4.00 mm |
7690 psi @Thickness 0.157 in |
2mm/min, injection molded, unannealed; ISO 178 |
| Flexural Modulus | 1.90 GPa @Thickness 4.00 mm |
276 ksi @Thickness 0.157 in |
2mm/min, injection molded, unannealed; ISO 178 |
| Izod Impact, Notched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C | 160 °F | ISO 75-1 |
| Vicat Softening Point | 103 °C | 217 °F | 120°C / 10N; ISO 306A |
| 191 °C | 376 °F | 50°C / 50N; ISO 306B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | |
| Mold Temperature | 25.0 - 70.0 °C | 77.0 - 158 °F | |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Dry Time | 2 - 3 hour | 2 - 3 hour |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S70Z Silicone Rubber
- Covestro Makrolon® DP 1-1265 Polycarbonate, Injection Grade (discontinued **)
- Huntsman HY 815 US Polyamide
- Lubrizol Advanced Materials Pearlthane® D91T86 Thermoplastic Polyurethane
- Samsung Cheil Industries Starex® WR-9330I Heat Resistant Grade ABS
- Zhejiang Juner JEPPBC001 Weatherability PP Series
- Ensinger Delrin® 150 Homopolymer Acetal (POM)
- Adell BR-14 Nylon 6, 20% Glass Reinforced
- Akzo Nobel Expancel® 461 WU 20 Wet unexpanded microspheres
- A. Schulman ComAlloy Hiloy® 243 SAN, Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved