Solvay TECHNYL® B 50 H1 PA66/6, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® B 50 H1 PA66/6, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL® B 50H1 is an unreinforced melamine cyanurate flame retarded copolyamide 66/6. This product has been heat stabilized and is suitable for injection molding. This product is available in natural, black, and in other colors upon request. Benefits: This phosphorus and halogen free flame retardant grade, UL94 V0 at 0.4mm, offers excellent filling qualities together with good stiffness.Available in: Asia Pacific, Europe, Latin America and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: Connectivity- junction blocks, terminal blocks, connectors…Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183/A |
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec |
1.1 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Viscosity | 25 cP @Shear Rate 100 1/s, Temperature 290 °C |
25 cP @Shear Rate 100 1/s, Temperature 554 °F |
|
| 27 cP @Shear Rate 1000 1/s, Temperature 290 °C |
27 cP @Shear Rate 1000 1/s, Temperature 554 °F |
||
| 29 cP @Shear Rate 1000 1/s, Temperature 270 °C |
29 cP @Shear Rate 1000 1/s, Temperature 518 °F |
||
| 30 cP @Shear Rate 1000 1/s, Temperature 260 °C |
30 cP @Shear Rate 1000 1/s, Temperature 500 °F |
||
| 107 cP @Shear Rate 100 1/s, Temperature 270 °C |
107 cP @Shear Rate 100 1/s, Temperature 518 °F |
||
| 109 cP @Shear Rate 100 1/s, Temperature 260 °C |
109 cP @Shear Rate 100 1/s, Temperature 500 °F |
||
| 109 cP @Shear Rate 10.0 1/s, Temperature 290 °C |
109 cP @Shear Rate 10.0 1/s, Temperature 554 °F |
||
| 120 cP @Shear Rate 10.0 1/s, Temperature 270 °C |
120 cP @Shear Rate 10.0 1/s, Temperature 518 °F |
||
| 130 cP @Shear Rate 10.0 1/s, Temperature 260 °C |
130 cP @Shear Rate 10.0 1/s, Temperature 500 °F |
||
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 Type 1A |
| Tensile Stress | 35.0 MPa @Strain 1.00 % |
5080 psi @Strain 1.00 % |
|
| 62.0 MPa @Strain 2.00 % |
8990 psi @Strain 2.00 % |
||
| 75.0 MPa @Strain 3.00 % |
10900 psi @Strain 3.00 % |
||
| 78.0 MPa @Strain 4.00 % |
11300 psi @Strain 4.00 % |
||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 type 1 A |
| 85.0 MPa | 12300 psi | ASTM D638 | |
| Elongation at Break | 10 % | 10 % | ISO 527 Type 1A |
| 10 % | 10 % | ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 type 1 A |
| Tensile Modulus | 3.60 GPa | 522 ksi | ISO 527 Type 1A |
| Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
| 120 MPa | 17400 psi | ASTM D790 | |
| Flexural Modulus | 3.65 GPa | 529 ksi | ISO 178 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 65.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
36.1 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 242 °C | 468 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ISO 75/Af |
| UL RTI, Electrical | 120 °C @Thickness 0.380 - 3.00 mm |
248 °F @Thickness 0.0150 - 0.118 in |
|
| UL RTI, Mechanical with Impact | 90.0 °C @Thickness 0.750 - 3.00 mm |
194 °F @Thickness 0.0295 - 0.118 in |
|
| Flammability, UL94 | V-0 @Thickness 0.380 mm |
V-0 @Thickness 0.0150 in |
1210 |
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
1210 | |
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
1210 | |
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
1210 | |
| Oxygen Index | 33 % | 33 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ignition temperature; ISO 60695-2-13 |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
ISO 60695-2-12 | |
| 960 °C @Thickness 1.60 mm |
1760 °F @Thickness 0.0630 in |
ISO 60695-2-12 | |
| 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.6 | 3.6 | IEC 60250 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243 |
| Dissipation Factor | 0.020 | 0.020 | IEC 60250 |
| Comparative Tracking Index | 575 V | 575 V | Solution B; IEC 60112 |
| 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 240 - 250 °C | 464 - 482 °F | |
| Front Barrel Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 245-255°C | |
| Fire and smoke F index | I2/F3 | NF F 16 101 |