Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
NYCOA 589 PA 6 FDA approved molding, extrusion and blown film gradeInformation provided by NYCOA, Inc. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
Nylene® 401D, Nylon 6 Injection molding grade. Dry as molded. Nylene 401D is a specially formulated nylon 6 molding resin possessing outstanding flow characteristics. Nylene 401D is ideally suited for applications requi.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
Nilit Polynil® C50 PA66/6 Co-Polymer Description: NYLON 66/6 copolymerApplication: CompoundingInformation provided by NILIT. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
Nilit Polynil® C50L Externally Lubricated PA66/6 Description: Polynil C50L shows better surface finish, flow and elongation than a comparable homopolymer. Key characteristics: Excellent flowHigh elongationGood impact strengthGood overall mechanica.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® DMX2415 PC (Asia Pacific) Lexan* DMX2415 is a polycarbonate resin with improved scratch resistance. Lexan* DMX2415 is available in transparent, translucent, and opaque colors.This data was supplied by SABIC-IP for the Asia P.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer Lexan* DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® DMX9455A PC Copolymer (Europe-Africa-Middle East) Lexan* DMX9455A is a standard flow, flame retardant, transparent polycarbonate copolymer resin with improved scratch resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle East r.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527-1/2 |
Radici Radilon® ALX14080 (dry) Nylon 66 Medium high viscosityInformation provided by Radici group. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 5271/2 |
Radici Radilon® S 37FL T Nylon 6 Radilon® S (homopolyamides) are normally used in cast and blown extrusion for the production of packaging films. Radilon® S grades can be extruded to a thickness varying from 20 mm to 100 mm.Appl.. |
|||
Tensile Strength, Yield | 80.0 - 152 MPa | 11600 - 22000 psi | Average value: 124 MPa Grade Count:9 |
Overview of materials for Polybutylene Terephthalate (PBT), 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 40% Glass Fiber Filled". Specific grades with glass content between 35.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer (Asia Pacific) This product will be phased out per January 2015 -- Lexan* DMX1435 is a UV stabilized standard flow polycarbonate copolymer resin with improved scratch resistance. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® DMX1435 PC Copolymer (Asia Pacific) This product will be phased out per January 2015 -- Lexan* DMX1435 is a UV stabilized standard flow polycarbonate copolymer resin with improved scratch resistance. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 2 in/min; ASTM D638 |
BASF Capron® B135QP Nylon 6 (DAM)
(discontinued **) Information provided by BASF Corporation.Capron® is no longer a part of the BASF standard line. The BASF nylon products have been consolidated in the Ultramid ® line. |
|||
Tensile Strength, Yield | 80.0 MPa @Strain 0.200 %, Temperature 982 °C |
11600 psi @Strain 0.200 %, Temperature 1800 °F |
|
Haynes R-41 alloy, 1.27 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, air cooled, aged 16 hours at 760°C (1400°F) Vacuum melted, exceptionally high strength at temperature between 649-982°C. Precipitation-hardening type, strength developed by various solutioning and aging heat treatments. Applications includ.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO-DIS 527 |
Schwartz Technical Plastics LAMIGAMID® 317 Cast Polyamide 6, Heat Stabilized, Dry Application: coupling parts, sealing rings, bearingsInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66 (Asia Pacific) LNP* Lubricomp* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added features of this material include: Internally Lubricated. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2312EPR PEI 30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics ULTEM 2312EPR PEI (Asia Pacific) 30% Milled glass filled, high flow Polyetherimide (Tg 217C) with internal mold release and enhanced electroplatability. ECO Conforming, UL94 V0 listing. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics Valox® ENH4530 PBT (Europe-Africa-Middle East) 15% GF PBT, Non-Brominated & Non-Chlorinated Flame retardant |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON ZE004 PPO LNP* STAT-KON* ZE004 is a compound based on PPO resin containing 20% Carbon Fiber. Added feature of this grade includes: Electrically Conductive. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 |
SABIC Innovative Plastics LNP Thermocomp KF003 Acetal Copoly LNP* Thermocomp* KF003 is a compound based on Acetal Copolymer resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO-DIS 527 |
Schwartz Technical Plastics OPTAMID® Cast Polyamide 6, Dry Application: deflection rope sheaves for elevatorsInformation provided by Schwartz Technical Plastics GmbH |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP 9X02841 PBT+PC LNP* Thermocmop* 9X02841 is a PBT/Polycarbonate blend containing proprietary fillers. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 |
Polyram Polytron P20B03 Polypropylene, 20% Long Glass Fiber A chemically coupled 20% long glass fibers reinforced black polypropylene, heat stabilized for injection molding applications.Information provided by Polyram. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | dry; ISO 527-1/-2 |
DSM Novamid® 1011CH5KR PA6 Heat Stabilized, Easy Molding Grade |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
Cresset Powers Cress-Alon™ A3000 3.0 r.v. Film or Extrusion Grade Nylon 6, Dry As Molded Neat resin, for film or extrusion.Information provided by Cresset Powers Ltd. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | conditioned; ISO 527-1/-2 |
EMS-Grivory Grivory® HT3Z black 9564 PA* Product description: Grivory HT3Z is an unreinforced and impact resistant, engineering thermoplastic based on semi crystalline partially aromatic copolyamide. This Grivory HT product is partially ba.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | dry; ISO 527-1/-2 |
EMS-Grivory Grivory® TSS/4 PA666 Product description: Grilon TSS/4 is an unreinforced, heat stabilized, normal viscosity PA66 + PA6 injection molding grade. Grilon TSS/4 has the following important properties: Good flow behaviorEas.. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
E-Polymers TEKAMID® TA210 LW TA210LW, Low Wear, Low Friction PA66, DAM Low wear, Low frictionInformation provided by E-Polymers Co. Ltd. |
|||
Tensile Strength, Yield | 80.0 MPa | 11600 psi | |
Radici Radilon® A HSK (dry) Nylon 66 Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information prov.. |