- Polymer Property : Flexural Strength = 120 MPa
Polymer Property : Flexural Strength = 120 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 120 MPa | 17400 psi | STN EN ISO 178 |
| Plastcom SLOVAMID 6 GF 15 T 25 Polyamide 6, 15% Glass Fiber, 25% Micronized Talc FeaturesGood anisotropy of the manufacturing shrinkage. The talc is added to get the material shrinkage identical in both directions. Application for flat products in disc form / no screw after co.. |
|||
| Flexural Strength | 120 MPa | 17400 psi | |
| Plastcom SLOVAMID 66 T 40 FRO 3 PA66, 40% mineral filling, flame retardant FeaturesPA 66 with the content of 40% chemically modified mineral filling a with fire retardant. Used for holders of electric hand tools, for hobby tools, gears, covers of electric tools, flat produ.. |
|||
| Flexural Strength | <= 120 MPa | <= 17400 psi | ISO 178 |
| Polykemi AB POLYabs T00 GF20 ABS, Glass Fibre-Reinforced Information provided by Polykemi AB |
|||
| Flexural Strength | 120 - 160 MPa | 17400 - 23200 psi | Injection; ISO 178 |
| Raschig Group 5563 DAP Glass-fiber reinforced diallyl phthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensiona.. |
|||
| Flexural Strength | <= 120 MPa | <= 17400 psi | ISO 178 |
| Polykemi AB SCANTEC PC S75R GF10 V0 Polycarbonate, Glass Fiber Reinforced, Flame Retardant Information provided by Polykemi AB |
|||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Celanese VECTRA E820iPd LCP, 40% Specialty
(Unverified Data**) Catalytically modified E820i40 % mineral , excellent flow, electrolytic metal platableA three-zone screw evenly divided into feed, compression, and metering zones is preferred. A higher percentage .. |
|||
| Flexural Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| Hexion Bakelite™ EP 8414 Epoxy Resin, High Arc Resistance, Improved Electrical Properties, Low Shrinkage
(dis Epoxy molding compound, inorganically filled, glass fiber reinforced, highly heat resistant, good electrical even at higher temperatures, very slight post shrinkage, increased media resistance, UL l.. |
|||
| Flexural Strength | 120 MPa @Temperature 22.0 °C |
17400 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
| Menzolit Menzolit® BMC 0390 Unsaturated Polyester UP BMC 0390 is a low profile DMC/BMC. Because of its low shrinkage, the material shows good surface quality as well as very low warpage. The product is suitable for applications if a better surface qua.. |
|||
| Flexural Strength | 120 MPa @Strain 5.50 % |
17400 psi @Strain 5.50 % |
d.a.m., 2 mm/min; ISO 178-A |
| Lanxess Durethan® B 30 S FN30 000000 Nylon 6, Flame Retardant PA 6, non-reinforced, injection molding, halogen free flame retardant, heat-aging resistanceInformation provided by LANXESS. |
|||
| Flexural Strength | 120 MPa | 17400 psi | |
| Lehmann & Voss LUVOCOM® 1106-8217 Polyether imide, with PTFE, lubricant modified Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Control disks, cams, slidi.. |
|||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Solvay TECHNYL® A 402 Natural FA PA66, DRY Description: Unreinforced polyamide PA66, very high viscosity, for extrusion.Available in: Europe and North AmericaProduct Applications: TECHNYL® A 402 NATURAL FA offers three main advantages: hi.. |
|||
| Flexural Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® 457 PBT (Europe-Africa-Middle East) VALOX 457 is a 6.5% glass fibre reinforced flame retarded PBT injection moulding resin. Applications: electrical and appliances industries. |
|||
| Flexural Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Valox® 771 PBT (Europe-Africa-Middle East) VALOX 771 is a 15% glass and 20% mineral filled, flame retarded injection moulding PBT resin. |
|||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Styrolution Luran® HD 20 SAN Luran HD 20 is an easy-flow grade of SAN especially designed for the medical market. It is suitable for moldings with very thin walls and / or adverse flow length to wall ratio. It features very goo.. |
|||
| Flexural Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| Sax Polymers SAXAMID 136F3Q32 Nylon 6, 15% Glass Fiber SAXAMID 136F3Q32 is a high-impact-modified polyamide 6 injection-molding-grade reinforced with 15% glass fibers with very high impact properties. Beside the high impact strength at low temperatures .. |
|||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Solvay TECHNYL® A 216 PA66, DRY Description: Unreinforced polyamide 66, medium viscosity, for injection molding.Available in: Asia Pacific and Latin AmericaProduct Applications: TECHNYL ® A 216 offers all of the primary propert.. |
|||
| Flexural Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics NORYL PPX PPX630 PPE+PP (Europe-Africa-Middle East) PPX630 is a 30% glass filled alloy of PP and PPO providing design freedom for applications requiring a wide range of stiffness, toughness and temperature. Generic identification acc. ISO11469: PP+PP.. |
|||
| Flexural Strength | 120 MPa | 17400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6 LNP* STAT-LOY* PF303 is a Nylon 6 base resin containing 15% Glass Fiber. Added features of this grade includes: Antistat. |
|||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Solvay TECHNYL® A 205F PA66, DRY Description: TECHNYL ® A 205F is an unreinforced polyamide 66 for injection molding. It is available in natural color.Benefits: The product offers two main advantages: excellent filling qualities.. |
|||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Unitika BV2120G15 PA66, 15% Glass Fiber Reinforced, Flame Retardant, Conditioned Information provided by Unitika Ltd. |
|||
| Flexural Strength | 120 - 130 MPa | 17400 - 18900 psi | At Rupture; ISO 178 |
| Vyncolit 4451 XB Novolac Phenolic Organic and mineral filled phenolic molding compound with excellent mechanical properties (highest notched impact strength).USES: Fuse holders, brush holders, circuit breakers, automotive ignition a.. |
|||
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Polyram PlusTek RA601 Nylon 6.6, Heat Resistant Heat resistant polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178-93 |
| Wellman Wellamid® GFT15N050-WBK 15% Glass Fiber Reinforced, Toughened, Weatherable Nylon 66 Description: Glass Fiber Reinforced, Toughened, Weatherable Nylon 66Information provided by Wellman. |
|||
| Flexural Strength | 120 MPa | 17400 psi | ASTM-D790 |
| Polyram RamTal PM3013G4 Acetal, 20% Glass Fiber 20% Glass fiber reinforced polyacetal for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Flexural Strength | 120 MPa @Diameter >=100 mm |
17400 psi @Diameter >=3.94 in |
24hr/23°C/50% RH; ISO 178; IEC/EN 61212-2 5.1 |
| Elektro-Isola Etronit IV C Phenolic, Paper Reinforcement, Yellow, Tubes Description: Suitable for electrical and mechanical applications where there is high air humidity. Lowest water absorption of all the Etronit types. Tropical grade. Good electrical properties at hig.. |
|||
| Flexural Strength | 120 MPa @Temperature 80.0 °C |
17400 psi @Temperature 176 °F |
ISO 178 |
| Celanese Celstran® PP-GF50-0405P10/10 PP, 50% Glass Reinforced Material code according to ISO 1043-1: PPInformation provided by Celanese |
|||
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Beijing Ranger Chem PBT 403 M-G10 HF Halogen Free Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
| Flexural Strength | 120 MPa @Temperature 80.0 °C |
17400 psi @Temperature 176 °F |
ISO 178 |
| Celanese Celstran® PP-GF40-0414 P10/10 PP, 40% Glass Reinforced Material code according to ISO 1043-1: PPInformation provided by Celanese |
|||
| Flexural Strength | 120 MPa | 17400 psi | cond.; ISO 178 |
| Azoty Tarnow™ Tarnamid® T-27 GF25 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 25% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning.. |
|||
| Flexural Strength | 120 MPa | 17400 psi | ASTM D 790 |
| RTP Company RTP 1199 X 117594 A Polyethylene Terephthalate (PET) Glass Fiber - Flame Retardant - Halogen Free |
|||