Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA), 33% Glass Fiber

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 30% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Amodel®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AS-1933 HS Polyphthalamide (PPA), 33% Glass Fiber.pdf
  Online Service   lookpolymers   27660005
Material Notes:
Amodel® AS-1933 HS is a 33% glass reinforced grade of polyphthalamide (PPA) resin developed specifically for improved performance in a 50/50 ethylene glycol and water environment. This material exceeds the performance required by the automotive industry for polymeric materials exposed to antifreeze at 226°F (108°C), even when tested at 275°F (135°C).Features: Antifreeze Resistant; Glycol Resistant; Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; Heat Stabilized; High Heat Resistance; High StrengthUses: Automotive Applications; Automotive Under the Hood; Housings; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal Replacement; Power/Other Tools; Thick-walled Parts; Valves/Valve PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications ASTM D4000 PA121 G35 Color: BK324 Black; ASTM D6779 PA121G35; BMW GS 93016 Color: BK 324 Black; BOSCH N28 BN05-OX1 BN0510-GF45-3Gsw01SO Color: BK324 Black; CHRYSLER MS-DB-478 CPN4116 Color: Black; FORD WSS-M4D861-A3 Color: BK324 Black; GM GMP.PPA.019 Color: Black; GM GMW16360P-PPA-GF35 Color: BK-324 Black; ISO 1874 PA6T/6I/66, MH, 12-120, GF33 Color: BK324 Black; PSA Peugeot-Citroën SPA X62 4203; VALEO PDT NVB 10 057 Color: BK324 BlackInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ISO 1183
Filler Content 33 %
33 %
Glass Fiber
Water Absorption 0.21 %

@Time 86400 sec
0.21 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 75.8 MPa
11000 psi
50 mm/min; ASTM D638
212 MPa
30700 psi
ISO 527-2
Elongation at Break 2.5 %
2.5 %
ISO 527-2
2.5 %
2.5 %
Tensile Modulus 7.58 GPa
1100 ksi
12.6 GPa
1830 ksi
ISO 527-2
Flexural Strength 309 MPa
44800 psi
ISO 178
Flexural Yield Strength 313 MPa
45400 psi
Flexural Modulus 10.6 GPa
1540 ksi
ISO 178
10.8 GPa
1570 ksi
Izod Impact, Notched (ISO) 9.50 kJ/m²
4.52 ft-lb/in²
Type 1, Notch A; ISO 180
Charpy Impact Unnotched 7.60 J/cm²
36.2 ft-lb/in²
Type 1, Edgewise; ISO 179
Charpy Impact, Notched 1.00 J/cm²
4.76 ft-lb/in²
Type 1, Edgewise; ISO 179
Thermal Properties Metric English Comments
Melting Point 312 °C
594 °F
ISO 11357-3
Deflection Temperature at 1.8 MPa (264 psi) 277 °C
531 °F
Unannealed; ASTM D648
278 °C
532 °F
Unannealed; Flatwise; ISO 75-2/A
Processing Properties Metric English Comments
Processing Temperature 79.4 °C
175 °F
Rear Barrel Temperature 304 - 318 °C
579 - 604 °F
Front Barrel Temperature 316 - 329 °C
601 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 135 °C
275 °F
Drying Temperature 121 °C

@Time 14400 sec
250 °F

@Time 4.00 hour
Moisture Content <= 0.10 %
<= 0.10 %
Descriptive Properties Value Comments
Additive Heat Stabilizer
Availability Africa & Middle East
Asia Pacific
Latin America
North America
Color Black
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant