DuPont Teijin Films Melinex® 547 Polyester Film, 400 Gauge
| Category | Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film |
| Manufacturer | DuPont Teijin Films (DTF) |
| Trade Name | Melinex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Teijin Films Melinex® 547 Polyester Film, 400 Gauge.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by DuPont.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 82.7 MPa | 12000 psi | ASTM D882A |
| Film Tensile Strength at Yield, TD | 82.7 MPa | 12000 psi | ASTM D882A |
| Film Elongation at Break, MD | 150 % | 150 % | ASTM D882A |
| Film Elongation at Break, TD | 100 % | 100 % | ASTM D882A |
| Coefficient of Friction, Dynamic | 0.50 | 0.50 | A-B; ASTM D1894 |
| Film Tensile Strength at Break, MD | 152 MPa | 22000 psi | ASTM D882A |
| Film Tensile Strength at Break, TD | 165 MPa | 24000 psi | ASTM D882A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 1.5 % @Temperature 190 °C, Time 300 sec |
1.5 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Shrinkage, TD | 0.00 % @Temperature 190 °C, Time 300 sec |
0.00 % @Temperature 374 °F, Time 0.0833 hour |
Unrestrained |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90.3 % | 90.3 % | TLT; ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Surface Roughness | .005 microns | Smooth side Ra |
| .083 microns | Rough side Ra |