SABIC Innovative Plastics LNP Stat-kon FX97333 PE (Asia Pacific)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Stat-kon FX97333 PE (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 0.990 g/cc
0.0358 lb/in³
ISO 1183
0.994 g/cc
0.0359 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.99 %
0.99 %
23°C / 50% RH; ISO 62
0.020 %

@Time 86400 sec
0.020 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.020 - 0.040 cm/cm

@Time 86400 sec
0.020 - 0.040 in/in

@Time 24.0 hour
ASTM D 955
0.020 - 0.040 cm/cm

@Time 86400 sec
0.020 - 0.040 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.020 - 0.040 cm/cm

@Time 86400 sec
0.020 - 0.040 in/in

@Time 24.0 hour
ASTM D 955
0.020 - 0.040 cm/cm

@Time 86400 sec
0.020 - 0.040 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 14.0 MPa
2030 psi
ISO 527
20.0 MPa
2900 psi
ASTM D 638
Tensile Strength, Yield 18.0 MPa
2610 psi
ISO 527
20.0 MPa
2900 psi
ASTM D 638
Elongation at Break 71.2 %
71.2 %
ISO 527
98.2 %
98.2 %
ASTM D 638
Elongation at Yield 17.6 %
17.6 %
ASTM D 638
19.6 %
19.6 %
ISO 527
Tensile Modulus 0.660 GPa
95.7 ksi
1 mm/min; ISO 527
0.810 GPa
117 ksi
50 mm/min; ASTM D 638
Flexural Strength 19.0 MPa
2760 psi
ASTM D 790
Flexural Modulus 0.630 GPa
91.4 ksi
ASTM D 790
Izod Impact, Notched 0.900 J/cm

@Temperature 23.0 °C
1.69 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 11.0 kJ/m²

@Temperature 23.0 °C
5.23 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 96.0 kJ/m²

@Temperature 23.0 °C
45.7 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 70.0 J
51.6 ft-lb
Multiaxial Impact; ISO 6603
30.0 J

@Temperature 23.0 °C
22.1 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 44.0 °C
111 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
44.0 °C

@Thickness 3.20 mm
111 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Volume Resistivity 100 ohm-cm - 1e+05
100 ohm-cm - 1e+05
ASTM D 257
Surface Resistance 100 ohm - 1e+05
100 ohm - 1e+05
ASTM D 257