Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 527 |
Polimeri Europa Eraclene® MR 80 High Density Polyethylene - Injection Molding Eraclene MR 80 is a high density polyethylene resin (HDPE) with antioxidants, suitable for injection molding application. Eraclene MR 80 shows a good balance between processability and mechanical p.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM 1457-62 T |
Fluorseals PTFE 60% bronze filled Improved compressive strength and thermal conductivity.Information provided by TEKU GmbH Fluorkunststoffe, a distributor of Fluorseals materials. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP FL003 PE LNP* LUBRICOMP* FL003 is a compound based on Polyethylene resin containing 15% PTFE. Added features include: Internally Lubricated. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCD861A PPE-TPE (Asia Pacific) Flexible, migration-improved, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO 527 |
SABIC Innovative Plastics LNP Stat-kon FX97333 PE LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for th.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D412 |
Sumitomo Chemical ESPOLEX® WT315 Thermoplastic Elastomer ESPOLEX® TPE Series is a group of thermoplastic elastomers produced by Sumitomo Chemical Company. Among its material advantages, ESPOLEX® TPE Series is distinguished by offering many low-densi.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
UBE Z322 Polyethylene Description: UBE Polyethylene is polymerized at high pressure using a tubular reactor. Production conditions are strictly controlled ensuring the product's superior physical and mechanical prope.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R527 |
Total FE 8004 LDPE blown film Radical polyethylene made by high pressure autoclave process. Advised temperature profile : 160 to 200°C.Information provided provided by Total Petrochemicals.Total Petrochemicals acquired former F.. |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds CL 75 Flexible PVC, Sheathing General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds FR 86 Flexible PVC, Insulation General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GA 80/2 Flexible PVC, Flame Retardant Sheathing General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GK 86/2 Flexible PVC, Flame Retardant Sheathing Lead Free General purposes |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R 527 |
Fainplast Compounds GS 70/T Flexible PVC, Injection Molding for Footwear Soles |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | IEC 60811 |
Fainplast Compounds HAX HF 018/13 Halogen Free PVC General purpose |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds HGK 80/2 Flexible PVC, Sheathing for High Temperatures Lead Free Operating temperature 90°C |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds HGKA 79/R Flexible PVC, Sheathing for High Temperatures Lead Free Sheathing oil resistent |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds CKL 80 Flexible PVC, Sheathing Lead Free General purposes |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ISO R 527 |
Fainplast Compounds GA 82 Flexible PVC, Flame Retardant Sheathing General purposes |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R 527 |
Fainplast Compounds MPH 57/T Medical Flexible PVC, Extrusion Extrusion and injection components no DOP |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R 527 |
Fainplast Compounds PH 65/A Flexible PVC, Transparent Extrusion Transparent profiles |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
Aclo Accutech Polypropylene Copolymer CP0437W20L1 Wollastonite Reinforced |
|||
Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | ASTM D4745-11 |
Adamas Adalon® 118 PTFE, 23/2% Carbon/Graphite Filled Information provided by Adamas, HPM |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
Arkema Group EVATANE® 28-25 Copolymer Ethylene - Vinyl Acetate EVATANE® 28-25 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 28-25 is stabilized with antioxidants. The High Vinyl Acetate co.. |
|||
Tensile Strength at Break | 14.0 - 24.0 MPa | 2030 - 3480 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 2500-20 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Highest flexibility. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical st.. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ASTM D638 |
Azdel SuperLite® SL551000-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness) AZDEL SuperLite® SL551000-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Tensile Strength at Break | 14.0 - 30.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2030 - 4350 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 31508 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Information provided by Solvay Specialty Polymers. |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | ISO R 527 |
Fainplast Compounds PH 70 Flexible PVC, Transparent Extrusion Transparent profiles and pipes |
|||
Tensile Strength at Break | 14.0 MPa | 2030 psi | 50 mm/min, 1A; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 5310 PP SABIC® PPcompound 5310 is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and heat stability with exterior automotive weathering stability. The IMDS I.. |