Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527 |
Polimeri Europa Clearflex® RN 50 U Linear Medium Density Polyethylene Clearflex RN 50 U is a linear medium density polyethylene resin, with antioxidants and UV stabilizers, suitable for rotomolding applications.Items manufactured with Clearflex RL 50 U show good mecha.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50 mm/min; ISO 527 |
Polimeri Europa Edistir SR 550 Polystyrene High impact, easy flow polystyrene with good elasticity at low temperatures.Suitable for injection moulding of large or complex parts with low thickness and high impact strength.
Designation: Thermo.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 Type IV |
Chevron Phillips Marlex® CL-200YNR JN (Natural) Rotational molding crosslinkable high density polyethylene
(d Benefits: crosslinks during molding - has outstanding melt strength at 204°C, is formulated to provide maximum UV protection for long-term outdoor weathering, contains an internal mold release, exc.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-2 |
Total Lacqtene® 2006 PBK 35 HDPE pipe, sheet
(discontinued **) LACQTENE® 2006 PBK 35 is a medium density polyethylene produced by the gas phase polymerization process with hexene as comonomer. LACQTENE® 2006 PBK 35 may be used for pipe extrusion (micro-irriga.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 Type IV |
Chevron Phillips Marlex® HHM TR-400G Medium density hexene copolymer
(discontinued **) Benefits: good processability, excellent melt strength, broad fusion range, outstanding stress cracking resistanceApplications: pond liners, gas and chemical tank containment liners, landfill liner.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
NOVA Chemicals Sclair® 8405 BK, 8405GBK MDPE Rotational Molding Resin
(discontinued **) Features: Good ESCR, high impact strength.Applications: Spray tanks.Data provided by the manufacturer. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
NOVA Chemicals Sclair® 8504 BK, 8504 GBK MDPE Rotational Molding Resin
(discontinued **) Features: Low melt index, excellent ESCR, high toughness at low temperatures.Applications: Large chemical storage tanks.Data provided by the manufacturer. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | 150x10x4 mm specimen, 50 mm/min; ISO 527-1/527-2 |
LyondellBasell SEQUEL® 1825 Engineered Polyolefin Description: SEQUEL® 1825 engineered polyolefin is designed for automotive applications that require energy management combined with ductility and a balance of stiffness and impact resistance ove.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50 mm/min; ASTM D638 |
ICO Polymers ICORENEâ„¢ 195-1331 LMDPE Rotational Molding Resin Description: ICORENE 195-1331 is a compounded linear medium density polyethylene copolymer developed for rotational molding. It has a good balance of properties such as toughness, easy flow and sti.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50 mm/min; ASTM D638 |
ICO Polymers ICORENEâ„¢ 324-3561 LMDPE Rotational Molding Resin Description: ICORENE 324-3561 is a linear medium density polyethylene developed for use in rotational molding. It has very good flow properties allowing the material to reproduce fine detail and me.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
LyondellBasell Astryn SZ021-2 Polypropylene Copolymer, 20% Talc Key Features: medium melt flow, medium modulus, mineral-filled, utility grade polypropylene copolymer, good impact and stiffness balance, versatileApplications: inner door panels and seat supportsDe.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-1, -2 |
LyondellBasell Hifaxâ„¢ CB285 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CB285 high melt flow, 1,300 MPa flexural modulus, low CLTE, UV-stabilized, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good balance of .. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 5521 PP SABIC® PPcompound 5521 is a mineral filled, impact modified polypropylene TPO. This material combines good flow with exterior automotive weathering stability. The general purpose black color prod.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics SABIC PPCOMPOUND 7450 PP SABIC® PPcompound 7450 is a mineral filled, impact modified polypropylene TPO. This material can exhibit high impact resistance and good paintability in automotive exterior applications. The IMDS.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | At 50 mm/min; ISO 527-2 |
Borealis Borcoat™ BB125E Polypropylene Adhesive for Steel Pipe Coating Borcoat BB125E is a chemically modified polypropylene copolymer designed to be used as the tie layer between the epoxy corrosion protection layer and the top-coat polypropylene Borcoat BB108E-1199.B.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | At 50 mm/min; ASTM D6883 IV |
Borealis Borecene™ RM8343PL Linear Polyethylene for Rotational Molding Borecene RM8343PL is plasma treated linear medium density natural polyethylene for rotational molding with improved adhesion properties. The material is plasma treated to change the chemical struct.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 2173HU Toyota High Impact Copolymer Polypropylene DescriptionPolyfort® PP 2173HU Toyota is a high flow, UV stabilized, high impact copolymer polypropylene.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
A. Schulman POLYFORT™ FXP 3000-3120 Glass Sphere Filled Copolymer Polypropylene DescriptionPolyfort® FXP 3000-3120 is a 30% glass sphere filled copolymer polypropylene compound.Information provided by A. Schulman. |
|||
Tensile Strength, Yield | 18.0 MPa @Strain 300 % |
2610 psi @Strain 300 % |
ISO 527-1/-2 |
Covestro Desmopan® W DP89043D Polyurethane PreprocessingMax. Water content |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ BNT 013 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for injection molded automotive interior applications such as door panels.Availability: Africa & Middle East, Asia Pacific, E.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
Aclo Accucomp Polypropylene CPO407L Copolymer |
|||
Tensile Strength, Yield | 18.0 - 27.0 MPa | 2610 - 3920 psi | Spec; ISO 527-1/2 |
Axion Polymers Axpoly® PS02 1010 Medium Impact Polystyrene PS02 Series polystyrenes offers the designer and processor a high performance polymer with well-defined properties in a range of options to suit many applications.The Axpoly® PS02 range of resin co.. |
|||
Tensile Strength, Yield | 18.0 MPa @Strain 50.0 % |
2610 psi @Strain 50.0 % |
50 mm/min |
Arkema Group Rilsan® BMV 400 TL Nylon 11 (Dry) Designation ISO 1874-PA11,M,18-002,ZFlexible grade for injection molding. Available color: natural. Light and heat stabilized. Plasticizing agent free.Outstanding impact strength and tear spreading .. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ASTM D638 |
NOVA Chemicals Sclair® 35BPM MDPE Extrusion Resin, 2.2% Carbon Black Filled
(discontinued **) Features: Excellent ESCR, medium molecular weight, good processability, excellent long term thermal stability, good chemical resistance, excellent UV stability.Applications: Extrusion on to metal pi.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | |
Trelleborg R721 Natural Rubber Polyisoprene All information provided by Trelleborg |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50mm/min; ISO 527-2 |
Borealis Daplen™ EF103AE Polypropylene TPO Compound Daplen™ EF103AE is a 10% mineral filled elastomer modified polypropylene compound intended for injection molding. This material has excellent balanced mechanical properties, high melt flow rate an.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | 150x10x4 mm specimen, 50 mm/min; ISO 527-1/527-2 |
Solvay Engineered Polymers DEXFLEX® 980HF TPO
(discontinued **) Description: DEXFLEX® 980HF is a thermoplastic olefinic elastomer (TPO) designed for large automotive exterior applications that require high flow for excellent processability, ductile impact prope.. |
|||
Tensile Strength, Yield | 18.0 MPa | 2610 psi | ISO 527-1, -2 |
LyondellBasell Hifax™ ETA3163/1 Thermoplastic Polyolefin Elastomer Description: Hifax™ ETA3163/1 medium melt flow, 900 MPa flexural modulus, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has an excellent balance of stiffness and low temper.. |