Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO 75 method A |
Quadrant EPP Cestilene™ HD 500 Polyethylene Data provided by Quadrant Engineering Plastic Products for polymers in their European product line. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO 75-1/-2 |
Quadrant EPP PE 500 PE-HMW, virgin (ISO Data) This grade exhibits a good combination of stiffness, toughness, mechanical damping ability with wear- and abrasion resistance and can easily be welded. In less demanding applications with respect to.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Compression Molded; ASTM D648 |
NOVA Chemicals Surpass® RMs244-UG Octene sHDPE Rotational Molding Film Features: Octene copolymerExceptional low temperature propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Standards 1.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Compression Molded; ASTM D648 |
NOVA Chemicals Surpass® RMs244-U Octene sHDPE Rotational Molding Film Features: Octene copolymerExceptional low temperature propertiesOutstanding stiffnessBroad processing windowSuperior whiteness for improved part appearanceEasy mold releaseNSF listed for Standards 1.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |
LyondellBasell Lupolen® 5031 L HDPE, Injection Molding Grade Easy flow, injection molding grade for closures, aerosol pumps, spray nozzles for spray cans, small automotive parts such as the caps on lead/acid batteries, knobs, barrels for writing instruments a.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |
LyondellBasell Lupolen® 5231 HX HDPE, Impact Grade Medium flow, impact resistant, very stress-crack resistant grade for closures, bottles that contain carbonated liquids, storage and tote boxes, as well as engineering components.Data was collected b.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |
LyondellBasell Lupolen® 5236 HX HDPE, Impact Grade Medium flow, impact resistant, high stress-crack resistant grade for closures for bottles that contain carbonated liquids. This product contains a slip agent.Data was collected by ISO methods and o.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |
LyondellBasell Lupolen® 5261 Z HDPE, Blow Molding Grade Relatively high viscosity blow molding grade for rigid, stackable and highly shock resistant containers for packaging all types of hazardous materials such as flammable, corrosive, poisonous and sur.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |
LyondellBasell Lupolen® 5261 Z HI HDPE Data was collected by ISO methods and originally provided by BASF. The Lupolen® product line is now produced by Basell. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP LUBRICOMP TX97446 PU LNP* LUBRICOMP* TX97446 is a compound based on Polyurethane containing Proprietary Fillers. Added feature of this material is: Wear Resistant. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C @Thickness 3.20 mm |
111 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR LNP THERMOCOMP* TH0600A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C @Thickness 3.20 mm |
111 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR (Asia Pacific) LNP THERMOCOMP* TH0600A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP THERMOCOMP TH0815A LNP* THERMOCOMP* TH0815A is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP THERMOCOMP TH0815A PUR (Asia Pacific) LNP* THERMOCOMP* TH0815A is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C @Thickness 3.20 mm |
111 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics LNP Stat-kon FX97333 PE LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for th.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
SABIC Innovative Plastics LNP Stat-kon FX97333 PE (Asia Pacific) LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for th.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C @Thickness 3.20 mm |
111 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
SABIC Innovative Plastics LNP Stat-kon FX97333 PE (Asia Pacific) LNP* Stat-kon* FX97333 is a compound based on Polyethylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for th.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Method A; ASTM D-648 |
Chevron Phillips Marlex® HMN TR-945/945G Polyethylene; HDPE High density polyethylene. These hexene copolymers are tailored for rotational molding applications that require: Wide process windows and excellent flowLong-term UV stabilizationGood impact stren.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 43.9 °C | 111 °F | ISO 75-2/A |
ExxonMobil Exxtral™ BNT 010 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive exterior painted parts such as bumper fascia.Availability: Africa & Middle East, Asia Pacific, Europe, South A.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | Unannealed; 54°C (129°F) annealed; ASTM Data |
Dow Prevail® 3050 ABS + Polyurethane PREVAIL® 3050 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used .. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 43.9 °C | 111 °F | |
Aclo Accucomp Polyethylene HD0202L High Density |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 43.9 °C | 111 °F | |
Aclo Accucomp Polypropylene CPO407L Copolymer |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM-D648 |
Braskem Prisma 2910 RACO Random Polypropylene Copolymer Prisma 2910 is a high melt flow rate random copolymer designed for injection molding applications. This product offers high impact strength at low temperatures and excellent processability. Its appl.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 - 127 °C | 111 - 260 °F | Average value: 82.7 °C Grade Count:8 |
Overview of materials for High Density Polyethylene (HDPE), Extruded This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Extruded". Each property range of values reported is minimum and maxim.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM D648 |
ALM PA 860 White Nylon 11 SLS Prototyping Polymer Unfilled White PA 11 that is formulated for easy processing across all LS platforms. Tightly controlled particle distribution creates a smooth surface finish and excellent feature detail. Parts prod.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ISO 75 |
LyondellBasell Hifax™ ETA-3163 Thermoplastic Olefin Resin Key Features: medium melt flow, medium high modulus, paintable thermoplastic elastomeric olefin resin, excellent impact and stiffness balance, good dimensional stability, good paintability, good pro.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | ASTM D648 |
A. Schulman POLYFORT™ PP 3701 Information provided by A. Schulman. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 44.0 - 150 °C | 111 - 302 °F | Average value: 69.7 °C Grade Count:192 |
Overview of materials for Polypropylene, Mineral Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values.. |