SABIC Innovative Plastics LNP LUBRICOMP RBL36XXJ PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RBL36XXJ PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RBL36XXJ is a compound based on Nylon 66 containing 30% Glass Bead, 15% PTFE. Added features of this grade include: Low Extractable, Healthcare, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.410 % | 0.410 % | 50% RH, 24 hrs; ASTM D570 |
| 0.580 % | 0.580 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D638 |
| 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 8.3 % | 8.3 % | 5 mm/min; ISO 527 |
| 10 % | 10 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 8.5 % | 8.5 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.93 GPa | 570 ksi | 1 mm/min; ISO 527 |
| 3.99 GPa | 579 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 107 MPa | 15500 psi | ISO 178 |
| Flexural Modulus | 3.56 GPa | 516 ksi | 2 mm/min; ISO 178 |
| 3.74 GPa | 542 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.510 J/cm | 0.955 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.35 J/cm | 8.15 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.47 | 0.47 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.44 | 0.44 | ASTM D3702 Modified |
| K (wear) Factor | 16.1 x 10-8 mm³/N-M | 8.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 82.6 x 10-8 mm³/N-M | 41.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 83.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 69.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 203 °C | 397 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 236 °C @Thickness 3.20 mm |
457 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C | 163 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 83.0 °C @Thickness 3.20 mm |
181 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nilit Polynil® P50FI Internally Lubricated Nylon 66
- Overview of materials for Polycarbonate, Carbon + PTFE Filled
- Mallard Creek Polymers ROVENE® 6017 Styrene-Acrylic Emulsion
- Techmer ES HiFill® PEI/C GF10 10% Glass Filled
- Techmer ES HiFill® PP 0159 B Polypropylene
- Styrolution Novodur® H702 ABS
- C.O.I.M. FILCO® 339 Film Former for Glass Fiber Sizes
- Austin Novel Materials Texalan® 564D Polyether-based TPU
- A. Schulman POLYFLAM™ FPP 1006S Talc Filled Homopolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved