Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527 |
Nilit FRIANYL A63 H-SG40 Nylon 6.6 for injection molding, 40% mineral filled Nylon 6.6 for injection molding, heat stabilized (dark natural color).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® EXL1413T PC Copolymer (Asia Pacific) Lexan* EXL1413T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 °C) ductility in combination with medium f.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® EXL1413T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1413T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 °C) ductility in combination with medium f.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® EXL1433T PC Copolymer (Asia Pacific) Lexan* EXL1433T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with .. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® EXL1433T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1433T polycarbonate (PC) siloxane copolymer resin is a UV stabilized transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with .. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® EXL1443T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1443T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance. This resin offers excellent low temperature (-30 C) ductility in co.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® EXL1463T PC Copolymer (Europe-Africa-Middle East) Lexan* EXL1463T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with medium flow ch.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® FXD121R PC Transparent/translucent PC for light diffusion special effects. MFR of 18.2. Color package may affect performance. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® FXD171R PC Transparent/transluscent PC for light diffusion special effects. MFR of 25.0.This data was supplied by SABIC-IP for the Americas region. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXM4701 PPC LEXAN FMX4701 is a high heat resistant poly(ester)carbonate injection molding resin. This grade is especially designed to visualize color effects.This data was supplied by SABIC-IP for the Americas .. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer High flow specialty polycarbonate with enhanced hemocompatibility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). E.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer High flow specialty polycarbonate with enhanced hemocompatibility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). E.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer (Europe-Africa-Middle East) High flow specialty polycarbonate with enhanced hemocompatibility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). E.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer (Europe-Africa-Middle East) High flow specialty polycarbonate with enhanced hemocompatibility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). E.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPX4 PC Copolymer Medium flow specialty polycarbonate - improved processability & autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPX4R PC Copolymer (Asia Pacific) Medium flow specialty polycarbonate with outstanding processability, ductility and autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatib.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® SLX2531T PC Copolymer (Asia Pacific) Transparent weatherable PC copolymer for blowmolding/extrusion. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | STN EN ISO 527-2 |
Plastcom SLOVAMID 6 LI/1 Polyamide 6, Impacted FeaturesPA 6 with the content of thermoplastic elastomer. Impacted, for mouldings with high toughness either at low temperatures, suitable for external use, eg. ski shoes, sports and safety helmets.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | |
Plastcom SLOVAMID 6 MI PA6, improved strength FeaturesPA 6 with the content of thermoplastic kaoutchouc. Impacted, for mouldings with high toughness either at minus temperatures, suitable for external use, eg. ski shoes, sports and safety helme.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy XTPM309E ASA+PC (Europe-Africa-Middle East) XTPM309E is a high heat resistant ASA+PC. It shows high impact retention, which can be positioned for various outdoor and indoor applications requiring superior heat aging properties and colour stab.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP RBL36XXJ PA 66 LNP* LUBRICOMP* RBL36XXJ is a compound based on Nylon 66 containing 30% Glass Bead, 15% PTFE. Added features of this grade include: Low Extractable, Healthcare, Wear Resistant. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DD0001 PC (Europe-Africa-Middle East) LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP Thermocomp PK0049 PA 6 (Europe-Africa-Middle East) LNP* THERMOCOMP* PK0049 is a compound based on PA 6 resin containing Glass Bead, Flame Retardant. Added features include; Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Mid.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xylex X7509UV PC+POLYESTER (Europe-Africa-Middle East) PC+POLYESTER, Transparent, UV-Stabilized,This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527-1/-2 |
Covestro Desmopan® DP 8410 Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527-1/-2 |
Covestro Desmopan® DP 8529 Polyurethane + ABS injection molding grademodified with ABSgood low-temperature flexibilitygood wear resistanceApplicationSki boot shellsAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
Chi Mei Kibisan® PN-117 SAN Injection Molding |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 |
Eurostar Staramide PB00A PA6, 50% Glass Bead Filled, Injection Molded Staramide PB00A is a 50% Glass Bead Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ASTM D638 |
Aclo Accutech ABS ABS834G40L Glass Reinforced |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® EXL1033C PC Copolymer Lexan*EXL1033C polycarbonate (PC) siloxane copolymer resin is a low flow, UV stabilized grade designed for (co)-extrusion. This resin offers low temperature (-30C) ductility and excellent extrusion .. |