Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® DMX1214 PC Copolymer (Europe-Africa-Middle East) This product will be phased out per January 2015 -- Lexan* DMX1214 resin is an improved flow, transparent copolycarbonate resin with improved scratch resistance. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® EXL1443T PC Copolymer (Asia Pacific) Lexan* EXL1443T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance. This resin offers excellent low temperature (-30 C) ductility in co.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer (Asia Pacific) High flow specialty polycarbonate with enhanced hemocompatibility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). E.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer (Asia Pacific) High flow specialty polycarbonate with enhanced hemocompatibility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). E.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPX4EU PC Copolymer (Europe-Africa-Middle East) Medium flow specialty polycarbonate - improved processability & autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® HPX4R PC Copolymer (Asia Pacific) Medium flow specialty polycarbonate with outstanding processability, ductility and autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatib.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® OQ4320 PC (Europe-Africa-Middle East) LEXAN OQ4320 is a medium viscosity grade with a UV cut-off up to 400 nm and a greater optical purity than standard grades. Fields of application for this material are optical lenses, f.i. in sunglas.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | STN EN ISO 527-2 |
Plastcom SLOVAMID 6 LI/1 Polyamide 6, Impacted FeaturesPA 6 with the content of thermoplastic elastomer. Impacted, for mouldings with high toughness either at low temperatures, suitable for external use, eg. ski shoes, sports and safety helmets.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Geloy XTPM309E ASA+PC (Europe-Africa-Middle East) XTPM309E is a high heat resistant ASA+PC. It shows high impact retention, which can be positioned for various outdoor and indoor applications requiring superior heat aging properties and colour stab.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Lexan® FXE1413T PC Copolymer (Asia Pacific) Clear PC-siloxane copolymer with excellent processability, for Visual fX capability in "Energy" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color packa.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics Lexan® FXM4701 PPC (Europe-Africa-Middle East) LEXAN FMX4701 is a high heat resistant poly(ester)carbonate injection molding resin. This grade is especially designed to visualize color effects.This data was supplied by SABIC-IP for the Europe-Af.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics Lexan® SLX2531T PC Copolymer Transparent weatherable PC copolymer for blowmolding/extrusion. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ASTM D638 |
LG Chemical LUCEL MR-310 Low Warpage POM, 10% Mineral Filled LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D638 |
SABIC Innovative Plastics LNP LUBRICOMP LL003 PEEK LNP* LUBRICOMP* LL003 is a compond based on Polyetheretherketone resin containing 15% PTFE Lubricant. Added feature of this material is: Wear Resistant. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP LUBRICOMP RBL36XXJ PA 66 LNP* LUBRICOMP* RBL36XXJ is a compound based on Nylon 66 containing 30% Glass Bead, 15% PTFE. Added features of this grade include: Low Extractable, Healthcare, Wear Resistant. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ASTM D638 |
SABIC Innovative Plastics LNP STAT-KON DD0001 PC (Europe-Africa-Middle East) LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON DD0001 PC (Europe-Africa-Middle East) LNP STAT-KON* DD0001 is a compound based on Polycarbonate resin containing Carbon Powder, Flame Retardant. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
SABIC Innovative Plastics Xylex X7509UV PC+POLYESTER (Asia Pacific) PC+POLYESTER, Transparent, UV-Stabilized,This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP AF002 ABS LNP THERMOCOMP* AF002 is a compound based on ABS resin containing 10% Glass Fiber. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP CX05470 PS LNP* THERMOCOMP* CX05470 is a compound based on Polystyrene resin containing 20% Glass Fiber. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP WFB54 PBT LNP* THERMOCOMP* WFB54 is a compound based on PBT resin containing 20% Glass Fiber, 25% Glass Bead. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 5 mm/min; ASTM D 638 |
SABIC Innovative Plastics LNP Lubricomp LL003E PEEK LNP* Lubricomp* LL003E is a compound based on Polyetheretherketone (PEEK) containing PTFE. Characteristics of this grade are: Easy Molding and Internally Lubricated.This data was supplied by SABIC.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL GTX GTX674PC PPE+PA6 A conductive PPE/PA blend designed to have improved surface appearance and elevated heat resistance for powder coating. The material is suitable for injection molding. The material is only availab.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL GTX GTX675 PPE+PA6 Noryl GTX* GTX675 Resin is a blend of Polyphenylene Ether(PPE) + Polyamide(PA) resin that is mineral filled, conductive, and suitable for injection molding. The conductivity level is optimized to a.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527-1/-2 |
Covestro Desmopan® DP 8410 Polyurethane As of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and officially adopted its new name – Covestro. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ISO 527-1/-2 |
Covestro Desmopan® DP 8529 Polyurethane + ABS injection molding grademodified with ABSgood low-temperature flexibilitygood wear resistanceApplicationSki boot shellsAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 |
Eurostar Staramide PB00A PA6, 50% Glass Bead Filled, Injection Molded Staramide PB00A is a 50% Glass Bead Reinforced, Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | 5 mm/min; ISO 527 |
Eurostar Starflam PK0049 PA6, Mineral Fiber Filled, Flame Retardant, Injection Molded Starflam PK0049 is a Free Flame Retardant Mineral Filled Polyamide 6 Injection Molding ResinInformation provided by Eurostar. |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ASTM D638 |
Aclo Accutech ABS ABS834G40L Glass Reinforced |
|||
Tensile Strength at Break | 64.0 MPa | 9280 psi | ASTM D638 |
Beijing Chemical Industry KAIFA® HN301-G0 PA6 Resin High flame retardant, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group) |