Nilit Polynil® P50FI Internally Lubricated Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer Nilit
Trade Name Polynil®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Nilit Polynil® P50FI Internally Lubricated Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Polynil P50 FI is an internally lubricated NYLON 66 with excellent flow characteristics and high elongation. It is widely used throughout many industries for applications that have long, thin flow lengths, like cable ties, connectors or industrial components.Key characteristics: Excellent flowHigh elongationGood mould release High toughness Good thermal performanceUL 94 V2 listed at 0.75 mmInformation provided by NILIT.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ASTM D792
Water Absorption 1.5 %
1.5 %
24h in H<sub>2</sub>O; sim. ISO 62
Water Absorption at Saturation 8.5 %
8.5 %
sim. ISO 62
Loss On Ignition 28 %
28 %
ASTM D2863
Viscosity Measurement 50
50
relative viscosity (formic acid); ASTM D789
Linear Mold Shrinkage, Flow 0.013 cm/cm
0.013 in/in
Nilit
Mechanical Properties Metric English Comments
Tensile Strength, Yield 81.01 MPa
11750 psi
ASTM D638
Elongation at Break 49 %
49 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Tensile Modulus 2.83 GPa
410 ksi
ASTM D638
Flexural Strength 122 MPa
17700 psi
ASTM D790
30.0 MPa

@Temperature 90.0 °C
4350 psi

@Temperature 194 °F
ASTM D790
Flexural Modulus 2.85 GPa
413 ksi
ASTM D790
0.800 GPa

@Temperature 90.0 °C
116 ksi

@Temperature 194 °F
ASTM D790
Izod Impact, Notched (ISO) 5.46 kJ/m²
2.60 ft-lb/in²
ASTM D256
4.41 kJ/m²

@Temperature -30.0 °C
2.10 ft-lb/in²

@Temperature -22.0 °F
ASTM D256
Charpy Impact Unnotched NB
NB
ISO 179
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179
0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 225 °C
437 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ASTM D648
Vicat Softening Point 240 °C
464 °F
49 N; ASTM D1525
255 °C
491 °F
9.8 N; ASTM D1525
Flammability, UL94 V-2

@Thickness 0.800 mm
V-2

@Thickness 0.0315 in
V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Dielectric Strength 18.0 kV/mm

@Thickness 2.00 mm
457 kV/in

@Thickness 0.0787 in
ASTM D149
Comparative Tracking Index >= 600 V
>= 600 V
UL 746
Descriptive Properties Value Comments
Heat Resistance - Ball Test OK
at 125°C, IEC 309
OK
at 165°C, IEC 309