SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal

Category	Polymer , Thermoplastic , Acetal (POM)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP LUBRICOMP* KP004 is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant.

Physical Properties	Metric	English	Comments
Density	1.48 g/cc	0.0535 lb/inÂ³	ASTM D792
	1.48 g/cc	0.0535 lb/inÂ³	ISO 1183
Moisture Absorption	0.180 %	0.180 %	50% RH, 24 hrs; ASTM D570
	0.430 %	0.430 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.021 - 0.029 cm/cm @Time 86400 sec	0.021 - 0.029 in/in @Time 24.0 hour	ASTM D955
Linear Mold Shrinkage, Transverse	0.021 - 0.029 cm/cm @Time 86400 sec	0.021 - 0.029 in/in @Time 24.0 hour	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	39.0 MPa	5660 psi	5 mm/min; ISO 527
	43.0 MPa	6240 psi	Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield	39.0 MPa	5660 psi	5 mm/min; ISO 527
	43.0 MPa	6240 psi	Type I, 5 mm/min; ASTM D638
Elongation at Break	30.3 %	30.3 %	Type I, 5 mm/min; ASTM D638
	42.8 %	42.8 %	5 mm/min; ISO 527
Elongation at Yield	13.7 %	13.7 %	Type I, 5 mm/min; ASTM D638
	21.5 %	21.5 %	5 mm/min; ISO 527
Tensile Modulus	1.83 GPa	265 ksi	50 mm/min; ASTM D638
	2.02 GPa	293 ksi	1 mm/min; ISO 527
Flexural Strength	60.0 MPa	8700 psi	ISO 178
	63.0 MPa	9140 psi	1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus	2.02 GPa	293 ksi	1.3 mm/min, 50 mm span; ASTM D790
	2.08 GPa	302 ksi	2 mm/min; ISO 178
Izod Impact, Notched	0.530 J/cm	0.993 ft-lb/in	ASTM D256
Izod Impact, Unnotched	6.19 J/cm	11.6 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	5.00 kJ/mÂ²	2.38 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	42.0 kJ/mÂ²	20.0 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	3.00 J	2.21 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	1.00 J	0.738 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.25	0.25	ASTM D3702 Modified
Coefficient of Friction, Static	0.14	0.14	ASTM D3702 Modified
K (wear) Factor	18.1 x 10^-8 mmÂ³/N-M	9.00 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	111 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	61.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
CTE, linear, Transverse to Flow	114 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	63.3 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi)	79.0 Â°C	174 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	87.0 Â°C @Thickness 3.20 mm	189 Â°F @Thickness 0.126 in	unannealed; ASTM D648