Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Strength | 60.0 MPa | 8700 psi | STN EN ISO 178 |
Plastcom SLOVAMID 66 HI Polyamide 66, Impact Grade FeaturesModified with thermoplastic reactive elastomer, determined for mouldings with high toughness also at low temperatures. Eligible application for ski-shoes, helmets for sport and other safety.. |
|||
Flexural Strength | 60.0 - 70.0 MPa | 8700 - 10200 psi | ASTM D790-03 |
Proto3000 Objet VeroBlue FullCure840 Rigid Opaque Prototyping Polymer Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid .. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Nilit FRIANYL A63 W Nylon 6.6 for injection molding Nylon 6.6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Strength | 60.0 - 70.0 MPa | 8700 - 10200 psi | Compression; ISO 178 |
Raschig Group 4552 Silicone Glass fiber reinforced silicone molding compound. Excellent thermal stability - up to +/- 300°C continuously, excellent electrical properties, good mechanical strength, very good dimensional stabi.. |
|||
Flexural Strength | 60.0 - 80.0 MPa | 8700 - 11600 psi | Compression; ISO 178 |
Raschig Group 6501 DAIP Glass-fiber reinforced diallyl isophthalate molding compound. Good mechanical strength together with retention of high electrical isolation properties under hot humid conditions, exceptional dimensi.. |
|||
Flexural Strength | 60.0 - 80.0 MPa | 8700 - 11600 psi | Compression; ISO 178 |
Raschig Group RALUPOL® 4566 UP Polyester Glass-fiber reinforced polyester molding compound. Low mold shrinkage and post-shrinkage, good electrical values, excellent heat resistance, outstanding pourability. This product meets the allowed u.. |
|||
Flexural Strength | 60.0 MPa @Temperature 100 °C |
8700 psi @Temperature 212 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, Dry as Molded
( AMODEL AP-9240 NL resin is a 40% mineral-filled, impact-modified polyphthalamide (PPA). It was designed to provide a smooth molded surface suitable for many decorative applications. This resin offer.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
Ineos Nova 1552 High Performance Styrenic Enhanced Polystyrene
(discontinued **) Easy processing, High modulus, Improve stress whitening, Custom colorsApplications: Injection molding, Office furniture, Electronic media, Photographic equipmentPerformance grades of polystyrene are.. |
|||
Flexural Strength | 60.0 MPa @Strain 3.50 %, Temperature 23.0 °C |
8700 psi @Strain 3.50 %, Temperature 73.4 °F |
ISO 178 |
DuPont Performance Polymers Delrin® 500T BK602 Acetal Homopolymer
(Unverified Data**) Delrin® 500T BK602 is a toughened, medium viscosity acetal homopolymer resin with impact resistance similar to Delrin® 100. It can be used in parts requiring noise reduction.Information provided b.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | |
Lehmann & Voss LUVOCOM® 80/TF/18/SI/2/BK Polyacetal-copolymer, with PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Emergency running property, gl.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | |
Lehmann & Voss LUVOCOM® 80-8444 Polyacetal-copolymer, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.dynamic stressReduced moment of inertia compared with metal parts.Isotropic shrinkage character.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | 2mm/min; ASTM D790 |
Kingfa HF-626 Flame Retardant ABS Features:UL 94 V-0 @ 1.6-3.0mm, 5VB @ 2.0mmHigh flowHigh impact resistanceApplications:Injection moldingMonitor cabinetCD-ROMPower switchInformation Provided by Kingfa Sci. & Tech. Co., Ltd. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | DIN 54352 |
Schwartz Technical Plastics LAMIGAMID® 200 Polyamide 66, Conditioned Application: bearing bushes, machine parts, gears, linersInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Styrolution Luran® S 797 S UV White 33999 Q455 ASA Description: Grade with especially high notched impact strengthApplications: Lighting covers and lawn mower housings.Information provided by STYROLUTION, which is a joint venture between BASF and IN.. |
|||
Flexural Strength | 60.0 MPa @Thickness 3.17 mm |
8700 psi @Thickness 0.125 in |
ASTM D790 |
Samsung Cheil Industries Starex® SD-0160 Super High Impact Grade ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
Samsung Cheil Industries Starex® WR-9140 General Purpose ABS Information provided by Polymer Technology and Services, LLC (PTS). |
|||
Flexural Strength | 60.0 MPa | 8700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP SH0700B PA12 LNP* Thermocomp* SH0700B is a compound based on Nylon 12 containing proprietary fillers. Added feature: High Specific Gravity |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
UBE UBESTA® 3024LU Rigid Black Electronic Grade Nylon 12 Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Unitika A3130HR-25 PA6, 25% Mineral Reinforced, Conditioned Information provided by Unitika Ltd. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178-93 |
Wellman Wellamid® XT1482-WT1 High Impact Nylon 66 Description: High Impact Nylon 66Information provided by Wellman. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ASTM D790 |
A. Schulman POLYFORT™ FPP 1285U Glass Filled, UV Stable Impact Copolymer Polypropylene DescriptionPolyfort® FPP 1285U is a 20% glass filled UV stable impact copolymer polypropylene product. Information provided by A. Schulman. |
|||
Flexural Strength | 60.0 MPa @Thickness 3.17 mm |
8700 psi @Thickness 0.125 in |
chs 0.05 in/min; 2 in span; ASTM D790 |
Diamond Polymers DIAMALOY GLY 7010 Sheet Extrusion Grade Diamaloy GLY 7010 resin is a high-gloss, high impact grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. It has good melt strength for extrusion and thermoforming, a.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | SAE J949 |
Azdel SuperLite® SL551800-100 PP Resin Matrix / 55% Glass Fiber (2 mm Molded Thickness) AZDEL SuperLite® SL551800-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Cathay PA511 Renewable Engineering Polyamide Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | 23°C, 50% RH; ASTM D790 |
Asahi Kasei Xyron® X0715 Modified Polyphenylene Ether AutomotiveInformation provided by Asahi Kasei |
|||
Flexural Strength | 60.0 - 80.0 MPa | 8700 - 11600 psi | |
Alliance BIN-55 Bonded (Composite) Magnetic Material |
|||
Flexural Strength | 60.0 MPa | 8700 psi | 2 mm/min; ISO 178 |
Chi Mei Polylac® PA-763A ABS - Flame Retardant F.R. High Heat |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
SABIC Innovative Plastics LNP Lubricomp CI001 PS (Asia Pacific) LNP* Lubricomp* CI001 is a compound based on Polystyrene resin containing Silicone. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Asia Pa.. |
|||
Flexural Strength | 60.0 MPa | 8700 psi | ISO 178 |
Polyram RamTal PM340S6 Polyacetal for Injection Molding, 30% Glass-Beads Filled 30% Glass-beads filled polyacetal for injection molding applications.Information provided by Polyram. |