Polymer Property : Flexural Modulus = 2.08 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 2.08 GPa
302 ksi
ASTM D790
PolyOne Geon™ HTX Ultra LA425 Polyvinyl Chloride Alloy (PVC Alloy)
Optimum for Black and Darker Colors below 50L value.Recommend drying material for a minimum of 2 hours at 160 degrees Farenheit. Ductile/Brittle transition as measured by Instrumented Impact is 5 de..
Flexural Modulus 2.08 GPa
302 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DX09407H PC
LNP* LUBRICOMP* DX09407H is a compound based on High Heat Polycarbonate containing proprietary fillers. Added features of this grade are: Wear Resistant, Healthcare.
Flexural Modulus 2.08 GPa
302 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal
LNP LUBRICOMP* KP004 is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Flexural Modulus 2.08 GPa
302 ksi
ISO 178
SABIC Innovative Plastics LNP LUBRICOMP KP004XXP Acetal Copolymer
LNP LUBRICOMP* KP004XXP is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Flexural Modulus 2.08 GPa
302 ksi
2 mm/min; ISO 178
SABIC Innovative Plastics LNP LUBRICOMP VN001 Super Tough Nylon
LNP* LUBRICOMP* VN001 is a compound based on Super Tough Nylon containing 2% MOS2. Added feature of th is grade is: Wear Resistant.
Flexural Modulus 2.08 GPa
302 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRILOY RX05498 PA 66
LNP LUBRILOY* RX05498 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: High Impact, Wear Resistant.
Flexural Modulus 2.08 GPa
302 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRILOY RX05498 PA 66 (Asia Pacific)
LNP LUBRILOY* RX05498 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: High Impact.
Flexural Modulus 2.08 GPa
302 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66
LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Flexural Modulus 2.08 GPa
302 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Asia Pacific)
LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Flexural Modulus 2.08 GPa
302 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRILOY RX99650 PA 66 (Europe-Africa-Middle East)
LNP LUBRILOY* RX99650 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Flexural Modulus 2.08 GPa
302 ksi
ASTM D 790
SABIC Innovative Plastics LNP Lubriloy Z2000 PPE+PS
LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP fo..
Flexural Modulus 2.08 GPa
302 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPE+PS (Asia Pacific)
LNP* Lubriloy* Z2000 is a compound based on PPE+PS Blend resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Flexural Modulus 2.08 GPa
302 ksi
ASTM D790
SABIC Innovative Plastics LNP LUBRILOY Z2000 PPO
LNP* LUBRILOY* Z2000 is a compound based on PPO resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.
Flexural Modulus 2.08 GPa
302 ksi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics Valox® K3501 PBT
Unfilled PBT, Hydrollytically Stable, Heat Stabilized, Impact Modified. A hydrollytically stable grade designed for improved performance under heat/humidity environments. Targeted at automotive unde..