Polymer Property : Tensile Strength at Break = 5660 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 MPa
5660 psi
Type I, 5 mm/min; ASTM D 638
SABIC Innovative Plastics Geloy EXGY30CP ASA
Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D638
SABIC Innovative Plastics LNP FARADEX AS003 ABS (Asia Pacific)
LNP* Faradex* AS003 is a compound based on Acrylonitrile Butadiene Styrene resin containing Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding.
Tensile Strength at Break 39.0 MPa
5660 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® HFD4271 PC
Lexan* HFD4271 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4271 has enhanced mold release, impact ductility..
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP AL001 ABS
LNP LUBRICOMP* AL-4010 HP is a compound based on Acrylonitrile Butadiene Styrene resin containing 5% PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D638
LG Chemical HI855H PMMA, Impact Resistant Grade
Molding granule designed for greater impact strength combined with the outstanding properties of conventional acrylic materialsFeatures: Excellent transparency and eleganceWeather resistance and che..
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D638-04
Ipiranga Petrochem MB 0310 MDPE
IPQ employs Spherilene technology from Basell in the production of MDPE. The raw materials, which are supplied by COPESUL, are pre-treated and fed into gas-phase reactors, where medium density polye..
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D638-02
Ipiranga Petrochem MB 0434 LS-L MDPE
IPQ employs Spherilene technology from Basell in the production of MDPE. The raw materials, which are supplied by COPESUL, are pre-treated and fed into gas-phase reactors, where medium density polye..
Tensile Strength at Break 39.0 MPa
5660 psi
ISO 527
SABIC Innovative Plastics LNP LUBRICOMP DP0039EF PC (Asia Pacific)
LNP* Lubricomp* DP0039EF is a compound based on Polycarbonate resin containing Silicone, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break 39.0 MPa
5660 psi
5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal
LNP LUBRICOMP* KP004 is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Tensile Strength at Break 39.0 MPa
5660 psi
ISO 527
SABIC Innovative Plastics LNP Stat-loy 9X05426C PMMA
LNP* Stat-loy* 9X05426C is a compound based on PMMA resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 39.0 MPa
5660 psi
ISO 527
SABIC Innovative Plastics LNP Stat-loy 9X05426C PMMA (Asia Pacific)
LNP* Stat-loy* 9X05426C is a compound based on PMMA resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Asia Pacific region.
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP MF001AS PP (Asia Pacific)
LNP* Thermocomp* MF001AS is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
Tensile Strength at Break 39.0 MPa
5660 psi
0.2 in/min; ASTM Test
Styrolution Terblend® N NM-12 ABS/PA6 (Dry)
Terblend N NM-12 is an ABS/PA6 blend combining high impact strength and rigidity with an excellent processability and surface appearance.Information provided by STYROLUTION, which is a joint venture..
Tensile Strength at Break 39.0 MPa
5660 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP V1000UXC PA
LNP* Thermotuf* V1000UXC is a compound based on Nylon resin. Added features of this material include: UV Stabilized.
Tensile Strength at Break 39.0 MPa
5660 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics NORYL PX1007 PPE+PS
Noryl* PX1007 is an unfilled non-chlorinated, non-brominated flame retardant PPE/HIPS grade.
Tensile Strength at Break 39.0 MPa
5660 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Valox® 364 PBT
Designed for outdoor telecommunications enclosure applications.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength at Break 39.0 MPa
5660 psi
50mm/min; ASTM D638
Denka TH-23 Transparent Resin Polymer (MBS resin) Polymethacrylate Butadiene Styrene
"TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Tensile Strength at Break 39.0 MPa
5660 psi
50 mm/min; ISO 527
Chi Mei Wonderloy® PC-345 PC/ABS Alloy
High Flow
Tensile Strength at Break 39.0 MPa
5660 psi
ISO R 527
Fainplast Compounds ARC 20 Rigid PVC, Atoxic for General Purpose
Bottles medium/high antishock
Tensile Strength at Break 39.0 MPa
5660 psi
Conditioned 15 days at 23°C - 50% RH; ASTM D638
Arkema Group Pebax® 3533 SA 01 MED Polyether Block Amide (PEBA)
Polyether block amide PEBAX® 3533 SA 01 MED is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This grade offers the highest quality and it is specially designed to meet t..
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D638-08
3M Scotchkote™ 2400 Pipe Renewal Liner
NSF/ANSI-61 certified polyurea formulation is 100% solids and contains no epoxy resin. It is designed to help solve a wide variety of problems common to potable water systems. It utilizes a trenchle..
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D638
Beijing Chemical Industry KAIFA® GL3200 ABS Flame-Retardant Grade
Good flammabilityInformation provided by Beijing Chemical Industry Research Institute (Group)
Tensile Strength at Break >= 39.0 MPa
>= 5660 psi
JIS K7127
Asahi Glass F-Clean® Film for Greenhouses
F-CLEAN®, produced by Asahi Glass Company, Ltd., is a Ethylene-Tetrafluoroethylene copolymer (ETFE) film used as the preferred covering material for horticultural greenhouses. High ten..
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D1457
Asahi Glass Fluon® CD123 PTFE Coagulated Dispersion Powder
Fluon®PTFE coagulated dispersion powders (fine powders) are used for paste extrusion to make tapes, tubes, rods and wire coatings.Information provided by Asahi Glass Company, Inc.
Tensile Strength at Break 39.0 MPa
5660 psi
ISO 527-2
Ascend Performance Materials Vydyne® 41H NT Nylon 66, Impact Modified, Conditioned
Vydyne® 41H NT is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyn..
Tensile Strength at Break 39.0 MPa
5660 psi
ISO 527-2
Ascend Performance Materials Vydyne® 41H Nylon 66, Impact Modified, Conditioned
Vydyne® 41H is a general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne..
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D412
Alliance Polymers Zythane™ 7090A Thermoplastic Polyurethane Elastomer
Zythane™ 7090A is a polyether-based TPU specifically formulated for extrusion molding applications .It exhibits excellent low compression set, abrasion resistance and toughness and has good hydroly..
Tensile Strength at Break 39.0 MPa
5660 psi
Z direction; ASTM D638
ALM FR 106 Nylon 11 SLS Prototyping Polymer
This flame retardant rapid prototyping material has additives in the raw material that allows it to pass aeronautic standard FAR25.853 smoke, flame, and toxicity tests. This material is ideal for Ae..
Tensile Strength at Break 39.0 MPa
5660 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Cycolac® DL100LG ABS (Europe-Africa-Middle East)
Cycolac DL100LG is a low gloss, high heat, high impact ABS/PC blend with low emission
Tensile Strength at Break 39.0 MPa
5660 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP DL004XXC PC
LNP* LUBRICOMP* DL004XXC is a compound based on Polycarbonate containing 20% PTFE. Characteristics of this grade are: Interrnally Lubricated.