Daikin DAI-EL G-755 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content

Category	Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer	Daikin Industries
Trade Name	DAI-EL
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Daikin DAI-EL G-755 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Features: Extrusion of hose and tubing, etc.Information provided by Daikin Industries.

Physical Properties	Metric	English	Comments
Specific Gravity	1.85 g/cc	1.85 g/cc	at 25°C
Mooney Viscosity	25 @Temperature 121 °C	25 @Temperature 250 °F	ML 1+10

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	66	66	Peak value, at 25°C
Tensile Strength at Break	14.5 MPa	2100 psi
Tensile Strength, Yield	2.30 MPa @Strain 100 %	334 psi @Strain 100 %
Elongation at Break	310 %	310 %
Tear Strength	21.6 kN/m	123 pli	at 25°C
Compression Set	15 %	15 %	70 hours at 25°C
	10 % @Temperature 100 °C	10 % @Temperature 212 °F	70 hours
	12 % @Temperature 175 °C	12 % @Temperature 347 °F	70 hours
	22 % @Temperature 200 °C	22 % @Temperature 392 °F	70 hours

Thermal Properties	Metric	English	Comments
Minimum Service Temperature, Air	-18.0 °C	-0.400 °F	TR test, TR10
	-15.5 °C	4.10 °F	Gehman torsion test, T10
	-8.50 °C	16.7 °F	Gehman torsion test, T2
	-8.00 °C	17.6 °F	TR test, TR70
Brittleness Temperature	-21.0 °C	-5.80 °F

Processing Properties	Metric	English	Comments
Processing Temperature	160 °C	320 °F	Cure Measuring Temperature
Cure Time	12.2 min	0.203 hour	Curelastmeter

Users viewing this material also viewed the following: