Polymer Property : Flexural Strength = 63.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Strength	63.0 MPa @Temperature 150 °C	9140 psi @Temperature 302 °F	ISO 178
Solvay Specialty Polymers Amodel® A-1340 HS Polyphthalamide (PPA) Resin, 40% Mineral/Glass Reinforced, Dry as Molded &a AMODEL® A-1340 HS is a 40% mineral/glass reinforced, heat stabilized polyphthalamide (PPA) which exhibits a high deflection temperature, high flexural modulus, high tensile strength and low warpage..
Flexural Strength	63.0 MPa	9140 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	63.0 MPa	9140 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Europe-Africa-Middle East) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	63.0 MPa	9140 psi	2mm/min; ASTM D790
Kingfa CPA-6 Toughened PA6 Features:High impactLow tendency to wrapApplications:Injection moldingSport applianceAutomobile partsPower toolsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Flexural Strength	63.0 MPa	9140 psi	5 mm/min; ISO 178
Gromax BTE45-DN00N1 Nylon 6 (Dry) Information provided by Gromax Enterprises Corp.
Flexural Strength	63.0 MPa	9140 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DL004 PC LNP* Lubricomp* DL004 is a compound based on Polycarbonate resin containing 20% PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	63.0 MPa	9140 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DL004 PC (Asia Pacific) LNP* Lubricomp* DL004 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	63.0 MPa	9140 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DZL34E PC LNP* Lubricomp* DZL34E is a compound based on Polycarbonate resin containing 20% Milled Glass, 15% PTFE. Added features of this material include: Internally Lubricated.
Flexural Strength	63.0 MPa	9140 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP KP004 Acetal LNP LUBRICOMP* KP004 is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant.
Flexural Strength	63.0 MPa	9140 psi	ISO 178
SABIC Innovative Plastics LNP STAT-LOY AF306 ABS (Asia Pacific) LNP* Stat-loy* AF306 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. Added features of this material include: Antistat.
Flexural Strength	63.0 MPa	9140 psi	ISO 178
SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas regi..
Flexural Strength	63.0 MPa	9140 psi	2 mm/min; ISO 178
Styrolution NovodurÂ® P2M-V ABS Pellets NovodurÂ® P2M-V has high impact strength, high gloss, and low emission. It is used for the production of molded plastic articles.
Flexural Strength	63.0 MPa	9140 psi	ASTM D790
SABIC Innovative Plastics NORYL PX2790 PPE+HIPS (Asia Pacific) PPE/HIPS unfilled FR-V1, 90C
Flexural Strength	63.0 MPa	9140 psi	ISO 178
SABIC Innovative Plastics LNP STAT-LOY NX13401 PC+ABS LNP* STAT-LOY* NX13401 is a compound based on PC+ABS blend. Added features of this material include: Antistat, Flame Retardant, Excellent Release.
Flexural Strength	63.0 MPa	9140 psi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOCOMP AB002 ABS LNP* THERMOCOMP* AB002 is a compound based on ABS resin containing 10% Glass Bead.
Flexural Strength	63.0 MPa	9140 psi	ASTM D 790
SABIC Innovative Plastics Noryl GTX GTX6010 PPE+PA6 (Asia Pacific) PA6 based unfilled GTX. High impact.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength	63.0 MPa	9140 psi	ASTM D790
Teknor Apex Sinpolene GPP1610 Polypropylene Availability: Africa & Middle East; Latin America; Asia Pacific; South America Additive: Glass Fiber Reinforcement, 10% Filler by Weight Features: Good Dimensional Stability; High Heat Resistance; ..
Flexural Strength	63.0 MPa	9140 psi	ASTM D790
Plenco 4466 Phenolic, Granular, Compression Molded PLENCO 04466 is a heat resistant, mineral and flock filled phenolic molding compound, offering excellent mechanical strength and cosmetic properties. UL recognized under component file E40654. 04466..
Flexural Strength	63.0 MPa	9140 psi	ASTM D790
Plenco 5350 Phenolic, Granular, Compression Molded PLENCO 05350 is a mineral and graphite filled phenolic molding compound, developed for seal applications. PLENCO 05350 offers excellent dimensional stability, lubricity, and low abrasion properties...
Flexural Strength	63.0 MPa	9140 psi	2mm/min; ASTM D790
Denka CL-430 Transparent Resin Polymer (MABS) ABS "TX Polymer" (methyl methacrylate styrene), MS resins as an alternative to acrylic resins, with low density, low moisture absorption, and good moldability, "TH Polymer/TP Polymer," MBS resins with a..
Flexural Strength	63.0 MPa	9140 psi	15mm/min; ASTM D790
Denka MALECCA K-700 ABS A heat-resistant ABS resin based on "DENKA IP" – a Styrene-N-Phenylmaleimide copolymer. It has been designed as an easy-to-use resin by improving conventional heat-resistant ABS resins which had de..
Flexural Strength	63.0 MPa	9140 psi	After conditioning at 23°C and 50% RH; ISO 178
Arkema Group Orgalloy® R 60 ES Polyamide Alloy Polyamide Alloy, Film and PackagingInformation provided by Arkema Group
Flexural Strength	63.0 MPa	9140 psi	After conditioning at 23°C and 50% RH; ISO 178
Arkema Group Orgalloy® RS 6000 Polyamide 6 Alloy Polyamide Alloy, Rigid grade, Nylon 6 basedTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group
Flexural Strength	63.0 MPa	9140 psi	ASTM D790
Aclo Accucomp ABS ABS801L Medium Impact Grade
Flexural Strength	63.0 MPa	9140 psi	ASTM D790
Aclo Accucomp ABS ABS802L High Impact Grade
Flexural Strength	63.0 MPa	9140 psi	23°C, 50% RH; ASTM D790
Asahi Kasei Xyron® X05516 Modified Polyphenylene Ether AutomotiveInformation provided by Asahi Kasei
Flexural Strength	63.0 MPa	9140 psi	ASTM D790
Beijing Chemical Industry KAIFA® GL3200 ABS Flame-Retardant Grade Good flammabilityInformation provided by Beijing Chemical Industry Research Institute (Group)
Flexural Strength	63.0 MPa	9140 psi	ASTM D790
A. Schulman ComAlloy Comtuf® 607 Nylon 6/6, Impact Modified, Flow Enhanced Data provided by the manufacturer, ComAlloy International Company. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has been integrated into the A Sc..
Flexural Strength	63.0 MPa	9140 psi	ISO 178
SABIC Innovative Plastics LNP LUBRICOMP DL004XXC PC LNP* LUBRICOMP* DL004XXC is a compound based on Polycarbonate containing 20% PTFE. Characteristics of this grade are: Interrnally Lubricated.