SABIC HP2022 Series Low Density Polyethylene for Blown Film

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer SABIC
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC HP2022 Series Low Density Polyethylene for Blown Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: HP2022 series resins are Low Density Polyethylene grades suitable for general purpose packaging. They exhibit better draw down, good optical and mechanical properties.HP2022N: No Slip & No AntiblockHP2022J: 750 ppm Slip & 1000 ppm AntiblockTypical Applications: Thin shrink film, lamination film, produce bags, textile packaging, general purpose bags with good optics and t-shirts carrier bags.Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ASTM D1505
Thickness 30.0 microns
1.18 mil
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ASTM D882
Film Tensile Strength at Yield, TD 7.00 MPa
1020 psi
ASTM D882
Film Elongation at Break, MD 290 %
290 %
ASTM D882
Film Elongation at Break, TD 570 %
570 %
ASTM D882
Elmendorf Tear Strength MD 180 g
180 g
ASTM D1922
Elmendorf Tear Strength TD 150 g
150 g
ASTM D1922
Elmendorf Tear Strength, MD 6.00 g/micron
152 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 5.00 g/micron
127 g/mil
ASTM D1922
Dart Drop 2.00 g/micron
50.8 g/mil
ASTM D1709
Dart Drop Test 60.0 g
0.132 lb
ASTM D1709
Film Tensile Strength at Break, MD 21.0 MPa
3050 psi
ASTM D882
Film Tensile Strength at Break, TD 18.0 MPa
2610 psi
ASTM D882
1% Secant Modulus, MD 160 MPa
23200 psi
ASTM D882
1% Secant Modulus, TD 180 MPa
26100 psi
ASTM D882
Thermal Properties Metric English Comments
Vicat Softening Point 92.0 °C
198 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 80 %
80 %
at 45°; ASTM D2457
Processing Properties Metric English Comments
Melt Temperature 160 - 180 °C
320 - 356 °F
Blow-up Ratio (BUR) 2.0 - 3.0
2.0 - 3.0