Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ISO 527-3
Polimeri Europa Clearflex® H&T FGH 196 Hexene Copolymer Linear Low Density Polyethylene
Clearflex H&T FGH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion.Films obtained from Clearflex H&T FGH ..
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ASTM D882
NOVA Chemicals Novapol® TF-0219-E Hexene LLDPE Film Resin
Exceptional toughens, Low gel levelApplications: Cast stretch wrapAdditives: High temperature A/OFilm properties are typical of cast film extruded at a melt temperature of 540°F, and a line speed o..
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ISO 527-3
Polimeri Europa Greenflex® FD 20 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion
Greenflex FD 20 is an ethylene vinyl acetate copolymer (EVA) suitable for blown film extrusion. Films produced with Greenflex FD 20 exhibit good optical properties, high impact resistance, tensile ..
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ISO 527-3
Polimeri Europa Greenflex® FD 23 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion
Greenflex FD 23 is an ethylene vinyl acetate copolymer (EVA) suitable for blown film extrusion. Greenflex FD 23 is a version of Greenflex FD 20 with added slip and antiblocking agents. Films produ..
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
at 2% offset; ASTM D882
ExxonMobil LD 145.PX Packaging Resin  (discontinued **)
LD 145.PX resin is a homopolymer cast film resin offering good clarity and toughness. Applications include Bread bags and other Food Packaging.Information provided by ExxonMobil Chemical
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ASTM D882
ExxonMobil Escorene® LD-144 EVA Film Resin  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.A 2% vinyl acetate copolymer packaging film resin. Film made from LD-144 offers improved impact strength and heat sealability compared to homopolym..
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
2 in per min; ASTM D882
Chevron Phillips MarFlex® D143 m-LLDPE Linear Low Density Polyethylene
Low Density PolyethyleneCustomer Benefits: This metallocene LLDPE film resin possesses the typical physical properties of metallocene polyethylenes with the added potential benefit of improved proce..
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ASTM D882
ExxonMobil Escorene® LL-3003 LLDPE/Hexene Premium Cast Stretch Film Resin  (discontinued **)
Data provided by the manufacturer, Exxon Chemical.A hexene copolymer LLDPE cast film resin. Films made from LL-3003 have outstanding tensile properties as well as stiffness and toughness.Applicatio..
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ISO 527-3
Polimeri Europa Clearflex® H&T CLH 196 Hexene Copolymer Linear Low Density Polyethylene
Clearflex H&T CLH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Stretch films manufactured with Clearflex H&T CLH 196 have..
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
500 mm/min; ISO 527-3
DuPont Elvaloy® 3107 AC Ethylene and 7% Butyl Acrylate Copolymer  (discontinued **)
Elvaloy® 3107 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3107 AC is developed to give films with good sealing properties, impact strength at lower temperature, and low shrinkag..
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ASTM D882
SABIC HP2022 Series Low Density Polyethylene for Blown Film
Product Description: HP2022 series resins are Low Density Polyethylene grades suitable for general purpose packaging. They exhibit better draw down, good optical and mechanical properties.HP2022N:..
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
500 mm/min; ISO 527-3
DuPont Elvaloy® 3108 AC Ethylene and 7% Butyl Acrylate Copolymer  (discontinued **)
Elvaloy® 3108 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3108 AC is developed to give films with good sealing properties, impact strength at lower temperature, and low shrinkag..