Polymer Property : Film Tensile Strength at Yield, TD = 7.00 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, TD	7.00 MPa	1020 psi	ISO 527-3
Polimeri Europa Clearflex® FG B3 Very Low Density Polyethylene Clearflex FG B3 is a linear low density polyethylene, with antioxidants, slip and antiblocking agents, suitable for blown film technology. The product is characterized by a very low density and a h..
Film Tensile Strength at Yield, TD	7.00 MPa	1020 psi	ISO 527-3
Polimeri Europa Greenflex® FL 25 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FL 25 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FL 25 show good optical properties and excellent sealability.Main Applications: ..
Film Tensile Strength at Yield, TD	7.00 MPa	1020 psi	ISO 527-3
Polimeri Europa Clearflex® CL B0 Very Low Density Polyethylene Clearflex CL B0 is a linear low density polyethylene, with antioxidants, characterized by a very low density (VLDPE).The resin has a high stretchability and a good cling effect.Main Applications: C..
Film Tensile Strength at Yield, TD	7.00 MPa	1020 psi	ISO 527-3
Polimeri Europa Clearflex® FG B0 Very Low Density Polyethylene Clearflex FG B0 is a linear low density polyethylene, with antioxidants, suitable for blown film technology.Films made with Clearflex FG B0 are highly transparent, have good sealing properties, even..
Film Tensile Strength at Yield, TD	7.00 MPa	1020 psi	ASTM D882
SABIC HP4023W Low Density Polyethylene for Blown Film Product Description: HP4023W is a Low Density Polyethylene grade suitable for producing general purpose films and contains slip and antiblock additives. It yields excellent processability with goo..
Film Tensile Strength at Yield, TD	7.00 MPa	1020 psi	ASTM D882
NOVA Chemicals Sclair® 10B Octene VLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, excellent sealability, excellent dart impact, excellent clarity.Applications: Co-extrusion.Data provided by the manufacturer.
Film Tensile Strength at Yield, TD	7.00 - 15.0 MPa	1020 - 2180 psi	Average value: 9.73 MPa Grade Count:24
Overview of materials for Linear Low Density Polyethylene (LLDPE), Blow Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "Linear Low Density Polyethylene (LLDPE), Blow Molding Grade". Each property range of values reported is ..
Film Tensile Strength at Yield, TD	7.00 MPa	1020 psi	500 mm/min; ISO 527-3
DuPont Elvaloy® 3107 AC Ethylene and 7% Butyl Acrylate Copolymer (discontinued **) Elvaloy® 3107 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3107 AC is developed to give films with good sealing properties, impact strength at lower temperature, and low shrinkag..
Film Tensile Strength at Yield, TD	7.00 MPa	1020 psi	ASTM D882
Westlake Hifor Xtreme SC74860-F Polyethylene (discontinued **) Hifor Xtreme Polyethylene SC74860-F is recommended for the core layer of cast stretch film. It provides excellent clarity and ultimate stretch values higher than the more conventional 2.0-2.5 MI cas..
Film Tensile Strength at Yield, TD	7.00 MPa	1020 psi	ASTM D882
SABIC HP2022 Series Low Density Polyethylene for Blown Film Product Description: HP2022 series resins are Low Density Polyethylene grades suitable for general purpose packaging. They exhibit better draw down, good optical and mechanical properties.HP2022N:..
Film Tensile Strength at Yield, TD	7.00 MPa	1020 psi	500 mm/min; ISO 527-3
DuPont Elvaloy® 3108 AC Ethylene and 7% Butyl Acrylate Copolymer (discontinued **) Elvaloy® 3108 AC contains antioxidant, slip and antiblock additives.Elvaloy® 3108 AC is developed to give films with good sealing properties, impact strength at lower temperature, and low shrinkag..