SABIC 218 Series Linear Low Density Polyethylene for Blown Film

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer	SABIC
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC 218 Series Linear Low Density Polyethylene for Blown Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: 218 series resins are Linear Low Density Polyethylene grades suitable for general purpose packaging. They are easy to process giving good tensile properties, impact strength and optical properties.218N: No Slip & No Antiblock218W: 1500 ppm Slip & 3500 ppm AntiblockTypical Applications: Lamination film, thin liners, shopping bags, carrier bags, coextruded films, consumer packaging, etc.Information provided by SABIC.

Physical Properties	Metric	English	Comments
Density	0.918 g/cc	0.0332 lb/in³	load density; ASTM D1505
Thickness	30.0 microns	1.18 mil
Melt Flow	2.0 g/10 min @Load 2.16 kg, Temperature 190 °C	2.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	12.0 MPa	1740 psi	ASTM D882
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
Film Elongation at Break, MD	700 %	700 %	ASTM D882
Film Elongation at Break, TD	750 %	750 %	ASTM D882
Elmendorf Tear Strength MD	130 g	130 g	ASTM D1922
Elmendorf Tear Strength TD	320 g	320 g	ASTM D1922
Elmendorf Tear Strength, MD	4.33 g/micron	110 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	10.67 g/micron	271.0 g/mil	ASTM D1922
Dart Drop Total Energy	630 J/cm	1.18 ft-lb/mil	Puncture Resistance; SABIC Method
Dart Drop	2.83 g/micron	71.9 g/mil	ASTM D1709
Dart Drop Test	85.0 g	0.187 lb	ASTM D1709
Film Tensile Strength at Break, MD	35.0 MPa	5080 psi	ASTM D882
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ASTM D882
1% Secant Modulus, MD	220 MPa	31900 psi	ASTM D882
1% Secant Modulus, TD	260 MPa	37700 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Vicat Softening Point	98.0 °C	208 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	13 %	13 %	ASTM D1003
Gloss	80 %	80 %	at 45°; ASTM D2457

Processing Properties	Metric	English	Comments
Melt Temperature	185 - 205 °C	365 - 401 °F
Blow-up Ratio (BUR)	2.0 - 3.0	2.0 - 3.0