Polymer Property : Film Tensile Strength at Yield, TD = 10.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ISO 527-3
Polimeri Europa Clearflex® CL 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex CL 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CL 106 are characterized by h..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ISO 527-3
Polimeri Europa Clearflex® FG 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex FG 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Clearflex FG 106 are characterized by ..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ISO 527-3
Polimeri Europa Clearflex® H&T CLH 108 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T CLH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films obtained from Clearflex H&T CLH 108 show e..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ISO 527-3
Polimeri Europa Clearflex® H&T CLH 150 Linear Low Density Polyethylene Clearflex H&T CLH 150 is a linear low density polyethylene resin, with antioxidants, suitable for cast film extrusion.Stretch films obtained from Clearflex H&T CLH 150 show good optical properties, ..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
SABIC 218 Series Linear Low Density Polyethylene for Blown Film Product Description: 218 series resins are Linear Low Density Polyethylene grades suitable for general purpose packaging. They are easy to process giving good tensile properties, impact strength a..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
SABIC 218B Linear Low Density Polyethylene for Cast Film Product Description: 218B is a Linear Low Density Polyethylene grade designed to provide easy processability and specially formulated for optimum thermal stability at high processing temperatures u..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ISO 527-3
Polimeri Europa Riblene® FL 24 Low Density Polyethylene - Blown Film Extrusion Riblene FL 24 is a low density polyethylene (LDPE) with added slip and antiblocking agents, suitable for blown film extrusion. Riblene FL 24 is characterized by a good balance between processabilit..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
NOVA Chemicals Novapol® LA-0424-A LDPE Foam Resin Good stiffness, Moderate toughness, Easy processabilityApplications: Industrial packaging, Liners, Blends with LLDPE, Foam articlesAdditives: Base resinFilm properties are typical of blown film extr..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
NOVA Chemicals Novapol® LF-Y320-D Fractional Melt LDPE Film Resin Features: High melt strength and superior bubble stabilityEnhances throughputs in LLDPE blendsSuperior strength and toughnessExcellent shrink film characteristics Applications: Industrial packagingL..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D 882
NOVA Chemicals Surpass® FPs021-F Octene sLLDPE Film Resin, 25 Micron Film FPs021-F complies with the U.S. FDA regulations for olefin polymers and may thus be used in the United States as an article or component of an article intended for use in contact with food.NOVA Chem..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ISO 527-3
Polimeri Europa Clearflex® FF 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex FF 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for blown film extrusion.Films manufactured with Clearflex FF 106 are characterized by ..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ISO 527-3
Polimeri Europa Clearflex® H&T CMH 108 Octene Copolymer Linear Low Density Polyethylene Clearflex H&T CMH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films obtained from Clearflex H&T CMH 108 show e..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	at 2% offset; ASTM D882
ExxonMobil LL 3301.34 Premium High Strength Film Resin (discontinued **) LL 3001 resins are hexene copolymer LLDPE film resins. Films produced from this resin have excellent tensile, toughness, and drawability properties. LL 3001 resins are available with blown film addi..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
Eastman 1925F Polyethylene Film (discontinued **) Polyethylene 1925F is a low density formulation with medium slip and medium antiblock. It is suggested for film applications that require heat-sealing treated-to-treated film surfaces and where good..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
Eastman E6838-795F Polyethylene (discontinued **) E6838-795F is a low density formulation with no slip or antiblock level. It is suggested for film applications that require a good balance of properties such as converter film for industrial packag..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D 882
Eastman E6838-923F Polyethylene (discontinued **) E6838-923F is a low density formulation with medium slip and medium antiblock. It is suggested for film applications that require heat-sealing treated-to-treated film surfaces and where good clarit..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
Eastman E6838-997F Polyethylene (discontinued **) E6838-997F natural is a low density formulation with no slip or antiblock. Outstanding optical properties make this material an excellent choice for calendering and as a clarity filler in co-extrud..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
ExxonMobil Escorene® LD-133 LDPE Packaging Film Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A homopolymer film resin with good clarity. It is suitable for processing in blown film equipment and can be drawn down to 1.0 mil.Applications: Fo..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
NOVA Chemicals Novapol® PF-0118-D Butene LLDPE Film Resin Film Properties. Features: Toughness and strength, thin films.Applications: Trash bags, garment film, bags-on-roll.Data provided by the manufacturer.
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
NOVA Chemicals Novapol® PF-0118-F Butene LLDPE Film Resin Film Properties. Features: Toughness and strength.Applications: Stretch wrap, blend resin, industrial packaging.Data provided by the manufacturer.
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
NOVA Chemicals Novapol® TF-Y822-CP Hexene LLDPE Film Resin Film Properties. Features: Good stiffness and machinability, exceptional toughness, suitable for narrow die gaps.Applications: Heavy duty sacks, high strength packaging.Data provided by the manufac..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
SCG Chemicals EL-Leneâ„¢ L1810F Linear Low Density Polyethylene Film Key Characteristics:High productivityGood optical propertiesContains 1600 ppm slip agent and 1900 ppm antiblocking agentRecommended Applications:Film for heavy duty bag, industrial bag, rice bag, su..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
SCG Chemicals EL-Leneâ„¢ LD1905FA Low Density Polyethylene Film Key Characteristics:High productivityGood optical propertiesCan be blended with HDPE and LDPE to improve tear resistance and seal strengthContains 1000 ppm slip agent and 700 ppm antiblocking agentR..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
Chevron Phillips MarFlex® D139FK Metallocene Linear Low Density Polyethylene, Blown Film This mLLDPE is tailored for applications that require:Excellent clarityExcellent glossExcellent toughnessExcellent heat sealTypical blown film applications include:Seal layer in coextrusionsHeavy du..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
Chevron Phillips MarFlex® D143FK Metallocene Linear Low Density Polyethylene, Blown Film This mLLDPE is tailored for applications that require:Excellent clarityExcellent glossExcellent toughnessExcellent heat sealTypical blown film applications include:Seal layer in coextrusionsHeavy du..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi
Dow DOWLEX™ 2045A Linear Low Density Polyethylene, Blown Film Grade DOWLEX® 2045A Polyethylene blown film extrusion resin is a premier film resin for heavy duty applications. It is utilized where improved thermal stability over a broader range of processing conditi..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
Dow FLEXOMER™ ETS-9066 NT 7, 2mil Very Low Density Polyethylene (VLDPE) Resin FLEXOMER™ ETS-9066 NT 7 is intended for use in single of multi-layer blown-film constructions or thick sheets. Films extruded from ETS-9064 NT 7 have a high tear strength, high impact strength, an..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
NOVA Chemicals Sclair® 11M1 Butene LLDPE Film Resin (discontinued **) Film Properties. Features: Low gel, strength and toughness.Applications: Co-extrusion.Data provided by the manufacturer.
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
NOVA Chemicals Sclair® 11H1 LLDPE Film Resin (discontinued **) Low gel, Excellent heat sealability, Easy processability, High toughness and strengthApplications: Heavy duty sack, High strength packagingAdditives: Process stabilizer, Polymer process aid, Antiblo..
Film Tensile Strength at Yield, TD	10.0 MPa	1450 psi	ASTM D882
Eastman E6838-963F Polyethylene (discontinued **) E6838-963F is a low density formulation with medium slip and medium antiblock. It is suggested for film applications that require a good balance of physical and optical properties.List of Applicati..