Polymer Property : Film Tensile Strength at Break, TD = 29.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ISO 527-3
Polimeri Europa Clearflex® CL 106 Hexene Copolymer Linear Low Density Polyethylene Clearflex CL 106 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion.Films manufactured with Clearflex CL 106 are characterized by h..
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ASTM D882
SABIC 218 Series Linear Low Density Polyethylene for Blown Film Product Description: 218 series resins are Linear Low Density Polyethylene grades suitable for general purpose packaging. They are easy to process giving good tensile properties, impact strength a..
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ISO 527-3
Polimeri Europa Greenflex® FF 45 Ethylene Vinyl Acetate Copolymer - Blown Film Extrusion Greenflex FF 45 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FF 45 show high toughness.Main Applications: Greenflex FF 45 is recommended for..
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ASTM D882
Petroquimica Triunfo Trilene® TS 8056 LLDPE-C8 and LDPE Blend The Trilene TS 8056 product is a blend with a high ratio of linear low-density polyethylene - octene comonomer (LLDPE-C8) with low-density polyethylene (LDPE) with elevated processability, ensuring ..
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ASTM D882
Petroquimica Triunfo Trilene® TS 8057 LLDPE-C4 and LDPE Blend The Trilene® TS 8057 product is a blend with a high ratio of linear low-density polyethylene - butene copolymer (LLDPE) with low-density polyethylene (LDPE) providing elevated processability and en..
Film Tensile Strength at Break, TD	29.0 MPa	4200 psi	ASTM D882
ExxonMobil Escorene® LD 767.MJ Cast and Compounding Film Resin (discontinued **) Escorene Ultra LD 767.MJ is a low gel 29.5% vinyl acetate copolymer designed for film and compounding applications.Information provided by ExxonMobil Chemical
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ASTM D882
LyondellBasell Montell 16502F3 Butene LLDPE Key Features: butene LLDPE resins for film extrusion applications, easy processing, low gels, good strength, no slip, no antiblockApplications: can liners and trash bags, blends, thin filmsMeets FDA..
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ASTM D882
LyondellBasell Montell 16502F7 Butene LLDPE Key Features: butene LLDPE resins for film extrusion applications, easy processing, low gels, good strength, low slip, medium antiblockApplications: can liners and trash bags, blends, thin filmsMeet..
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ASTM D882
LyondellBasell Montell 16502F8 Butene LLDPE Key Features: butene LLDPE resins for film extrusion applications, easy processing, low gels, good strength, medium slip, high antiblockApplications: can liners and trash bags, blends, thin filmsMee..
Film Tensile Strength at Break, TD	29.0 MPa	4200 psi	ASTM D882
LyondellBasell PetrotheneÂ® GA601031 Linear Low Density Polyethylene ApplicationsPETROTHENEÂ® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene..
Film Tensile Strength at Break, TD	29.0 MPa	4200 psi	ASTM D882
LyondellBasell PetrotheneÂ® GA601032 Linear Low Density Polyethylene ApplicationsPETROTHENEÂ® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene..
Film Tensile Strength at Break, TD	29.0 MPa	4200 psi	ASTM D882
LyondellBasell PetrotheneÂ® GA601033 Linear Low Density Polyethylene ApplicationsPETROTHENEÂ® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene..
Film Tensile Strength at Break, TD	29.0 MPa	4200 psi	ASTM D882
LyondellBasell PetrotheneÂ® NA285003 Medium Density Polyethylene ApplicationsPETROTHENE NA 285-003 is a medium density polyethylene resin for blown or cast film extrusion. Typical applications include overwrap film. This product exhibits good film optics and hi..
Film Tensile Strength at Break, TD	29.0 MPa	4200 psi	ASTM D882
LyondellBasell PetrotheneÂ® GA601030 Linear Low Density Polyethylene ApplicationsPETROTHENEÂ® GA 601 series are pelletized, linear low density polyethylenes for applications requiring maximum strength and toughness. These products offer excellent additive homogene..
Film Tensile Strength at Break, TD	29.0 MPa	4200 psi	ASTM D882
LyondellBasell PetrotheneÂ® LP540200 High Density Polyethylene ApplicationsPETROTHENE LP 5402-00 is a copolymer resin designed for blown film applications. This resin offers high stiffness, excellent appearance and bubble stability and good draw-down. LP 5402-0..
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi
UBE 1022FDX23 Nylon 6 Homopolymer Film Specialties: High slip typeProcessing: Water cooling processTypical applications: small pouch & generalInformation provided by UBE.
Film Tensile Strength at Break, TD	29.0 MPa	4200 psi	ASTM D882
ExxonMobil Escorene™ UL 00112 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: UL 00112 is a fractional MI copolymer of ethylene and vinyl acetate.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: No Thermal Stabilizer: No Applica..
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	Calculated from mfr's report of 78 N/cm per ASTM D828 and the typical thickness
DuPont™ Nomex® 418 Paper, 10 mil Nominal Thickness Nomex® Type 418 is designed for high-voltage applications such as motor conductor and coil wrap, transformer ground and layer insulation. It can be readily impregnated with varnishes. This calen..
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi
Dow DOWLEX™ 2101 Linear Low Density Polyethylene, Blown Film Grade DOWLEX® 2101 Polyethylene resin, a general purpose blown film extrusion resin, is an excellent choice for high speed, thin gauge film applications. It contains medium levels of both slip additive a..
Film Tensile Strength at Break, TD	29.0 MPa	4210 psi	ASTM D882
Braskem LL 218/21 LLDPE Blown Film Extrusion Polyethylene 38µm film gauge, obtained in 40mm extruder, with blow up ratio 2, 2:1Applications: Automatic packaging (FFS); "liners"; general purpose; HDPE and LDPE blends. Information provided by Braskem
Film Tensile Strength at Break, TD	29.0 - 303 MPa	4210 - 44000 psi	Average value: 128 MPa Grade Count:21
Overview of materials for Nylon 6, Film Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Film Grade". Each property range of values reported is minimum and maximum values of appropriat..
Film Tensile Strength at Break, TD	29.0 MPa	4200 psi	ASTM D882
ExxonMobil Escorene™ FL 00112 Ethylene Vinyl Acetate Copolymer (European Grade) Product Description: FL 00112 is a copolymer of ethylene and vinyl acetate offering low gel. Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: No App..