Overview of materials for Polyphenylene Sulfide (PPS), Aramid Fiber

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Aramid Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Sulfide (PPS), Aramid Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Aramid Fiber". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.25 - 1.56 g/cc
0.0452 - 0.0564 lb/in³
Average value: 1.41 g/cc Grade Count:23
Filler Content 10.0 - 30.0 %
10.0 - 30.0 %
Average value: 16.3 % Grade Count:8
Water Absorption 0.0200 - 0.200 %
0.0200 - 0.200 %
Average value: 0.0930 % Grade Count:10
Linear Mold Shrinkage 0.000500 - 0.0140 cm/cm
0.000500 - 0.0140 in/in
Average value: 0.00686 cm/cm Grade Count:22
Mechanical Properties Metric English Comments
Hardness, Rockwell R 123
123
Average value: 123 Grade Count:3
Tensile Strength, Ultimate 45.0 - 134 MPa
6530 - 19500 psi
Average value: 76.3 MPa Grade Count:23
Elongation at Break 1.00 - 4.00 %
1.00 - 4.00 %
Average value: 1.62 % Grade Count:19
Elongation at Yield 1.60 - 2.60 %
1.60 - 2.60 %
Average value: 2.08 % Grade Count:4
Modulus of Elasticity 3.80 - 22.8 GPa
551 - 3300 ksi
Average value: 7.88 GPa Grade Count:23
Flexural Yield Strength 85.0 - 214 MPa
12300 - 31000 psi
Average value: 124 MPa Grade Count:22
Flexural Modulus 3.50 - 20.7 GPa
508 - 3000 ksi
Average value: 7.28 GPa Grade Count:22
Izod Impact, Notched 0.214 - 1.28 J/cm
0.400 - 2.40 ft-lb/in
Average value: 0.364 J/cm Grade Count:16
Izod Impact, Unnotched 1.07 - 3.20 J/cm
2.00 - 6.00 ft-lb/in
Average value: 1.90 J/cm Grade Count:16
Charpy Impact Unnotched 0.500 - 1.20 J/cm²
2.38 - 5.71 ft-lb/in²
Average value: 0.975 J/cm² Grade Count:4
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 220 - 240 °C
428 - 464 °F
Average value: 230 °C Grade Count:4
Deflection Temperature at 0.46 MPa (66 psi) 249 - 271 °C
480 - 520 °F
Average value: 258 °C Grade Count:5
Deflection Temperature at 1.8 MPa (264 psi) 110 - 260 °C
230 - 500 °F
Average value: 206 °C Grade Count:17
Flammability, UL94 V-0
V-0
Grade Count:16
Electrical Properties Metric English Comments
Electrical Resistivity 1000 - 1.00e+16 ohm-cm
1000 - 1.00e+16 ohm-cm
Average value: 5.11e+15 ohm-cm Grade Count:11
Surface Resistance 1.00e+7 - 1.00e+14 ohm
1.00e+7 - 1.00e+14 ohm
Average value: 1.49e+13 ohm Grade Count:7
Insulation Resistance 1.00e+12 ohm
1.00e+12 ohm
Average value: 1.00e+12 ohm Grade Count:4
Processing Properties Metric English Comments
Processing Temperature 140 - 330 °C
284 - 626 °F
Average value: 300 °C Grade Count:11
Nozzle Temperature 320 - 340 °C
608 - 644 °F
Average value: 330 °C Grade Count:4
Melt Temperature 70.0 - 343 °C
158 - 650 °F
Average value: 307 °C Grade Count:15
Mold Temperature 65.6 - 180 °C
150 - 356 °F
Average value: 155 °C Grade Count:20
Drying Temperature 50.0 - 150 °C
122 - 302 °F
Average value: 122 °C Grade Count:15
Moisture Content 0.0200 - 0.0400 %
0.0200 - 0.0400 %
Average value: 0.0371 % Grade Count:7
Injection Pressure 68.9 - 138 MPa
10000 - 20000 psi
Average value: 89.6 MPa Grade Count:15