Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 3.80 - 6.00 GPa @Temperature 60.0 - 120 °C |
551 - 870 ksi @Temperature 140 - 248 °F |
Average value: 4.83 GPa Grade Count:2 |
Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E.. |
|||
Modulus of Elasticity | 3.80 - 10.5 GPa | 551 - 1520 ksi | Average value: 7.73 GPa Grade Count:38 |
Overview of materials for Polycarbonate, 30% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 30% Glass Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Modulus of Elasticity | 3.80 - 22.8 GPa | 551 - 3300 ksi | Average value: 7.88 GPa Grade Count:23 |
Overview of materials for Polyphenylene Sulfide (PPS), Aramid Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS), Aramid Fiber". Each property range of values reported is minimum and maximu.. |
|||
Modulus of Elasticity | 3.80 - 18.25 GPa @Temperature -40.0 - 150 °C |
551 - 2647 ksi @Temperature -40.0 - 302 °F |
Average value: 10.1 GPa Grade Count:5 |
Overview of materials for Nylon 6, 50% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 50% Glass Fiber Filled". Specific grades with glass content between 45% and 54% are included. E.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | |
Lehmann & Voss LUVOCOM® 1106-7940/GY/EM Polyether imide, unreinforced, laser markable Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | |
Lehmann & Voss LUVOCOM® 1500-0871 Polysulfone, with glass spheres Applications: Isotropic shrinkage characteristics.Chemical and hydrolysis resistance parts, non flammable.High dimensionally stable precision parts, high continuous use temperature.Control disks, ca.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | |
Lehmann & Voss LUVOCOM® 1/GK/30/TF/13/SI/2 Polyamide 66, with glass spheres, PTFE, lubricant modified, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Low warpage, isotropic shrinka.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | |
Lehmann & Voss LUVOCOM® 1106-8232 Polyether imide, unreinforced, laser markable Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | ISO 527-2 |
Tisan TISOPLEN® 40% Talc Filled Heat Stabilized Homopolymer Polypropylene TISOPLEN has a wide area of application in furniture, durable goods, household appliances, electrics/electronics, and telecommunication industries. General specifications include Low densityLow mois.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | |
Toyobo ECOVYLOPET® EMC2301E PET Bottle Recycling Grade, 15% Filler Reinforced Features: PET Bottle Recycling Grade, 15% Filler Reinforced, Modified TypeApplications: Automobile engine head coversHot platesVending machine partsUmbrella ribsInformation provided by Toyobo. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 20MB668 OPP Film Product Description: Bicor 20MB668 is a high speed transparent, biaxially oriented polypropylene film, coated one side acrylic, one side very low temperature seal (VLTS) coating. VLTS coating provid.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 21MB777 OPP Film Product Description: Bicor 21MB777 is a high gas barrier, biaxially oriented transparent PP film coated one side PVdC, one side acrylic. This film provides outstanding performance on all packaging m.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 25ICT OPP Film Product Description: A one-side sealable, very broad seal range coextruded BOPP. This film is designed for use in unsupported plain or surface printed high-speed horizontal applications. The enhance.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 25MB668 OPP Film Product Description: A high speed transparent, biaxially oriented polypropylene film, coated one side acrylic, one side very low seal temperature (VLTS) coating. VLTS coating provides excellent perf.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 25MBT666 OPP Film Product Description: Biaxially oriented polypropylene film, acrylic coated two sides. This film is specifically suitable for unsupported overwrapping offering unique aspect and cost reduction advant.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 26MB777 OPP Film Product Description: A high gas barrier, biaxially oriented transparent polypropylene film, coated on one side PVdC, one side acrylic. This film provides outstanding performance on all packaging mac.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 30MB668 OPP Film Product Description: A high speed transparent, biaxially oriented polypropylene film, coated one side very low temperature seal (VLTS) coating. VLTS coating provides excellent performances on high s.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 32MB777 OPP Film Product Description: A high gas barrier, biaxially oriented transparent polypropylene film, coated one side PVdC, one side acrylic. This film provides outstanding performance on all packaging machin.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | ISO 527 |
DSM Fibre Intermediates Nyrim® 2025 (Wollastocoat®), Dry Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is processed via Reaction Injection Moulding (RIM) tec.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 30MBT666 OPP Film Product Description: A biaxially oriented transparent polypropylene film, acrylic coated two sides. This film is specifically suitable for unsupported overwrapping, offering unique aspect and cost r.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | ISO 178 |
Addiplast Addinyl B2 ZG30 Nylon 6, 30% Glass Bead Glass bead reinforced, improved stiffness and dimensional stability, increased thermal aging stabilityInformation provided by Addiplast. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | Conditioned; ISO 178 |
Addiplast Addilene J 490 M40S Flame Retardant Polypropylene, 40% Mineral Filled Flame retardant, mineral filled, with halogensInformation provided by Addiplast. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | ISO 178 |
Addiplast Addinyl A2 G30 Nylon 66, 30% Glass Bead Glass bead reinforced, improved stiffness and dimensional stabilityInformation provided by Addiplast. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | ISO 178 |
Addiplast Addinyl A2 ZG30 Nylon 66, 30% Glass Bead Glass bead reinforced, improved stiffness and dimensional stability, increased thermal aging stabilityInformation provided by Addiplast. |
|||
Modulus of Elasticity | 3.80 - 5.20 GPa | 551 - 754 ksi | Average value: 4.73 GPa Grade Count:3 |
Overview of materials for Polycarbonate, Glass Fiber & Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Glass Fiber & Bead Filled". Each property range of values reported is minimum and maximum.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | TD; ExxonMobil Method |
ExxonMobil Bicor™ 20MBT666 OPP Film Product Description: Bicor 20MBT666 is a biaxially oriented transparent polypropylene film acrylic coated two sides. This film is specifically suitable for unprinted overwrapping, offering unique as.. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | ISO 178 |
Addiplast Addinyl B2 G30 Nylon 6, 30% Glass Bead Glass bead reinforced, improved stiffness and dimensional stabilityInformation provided by Addiplast. |
|||
Modulus of Elasticity | 3.80 - 10.6 GPa | 551 - 1540 ksi | Average value: 6.83 GPa Grade Count:4 |
Overview of materials for Polystyrene + Polyphenylene Ether, Glass Filler This property data is a summary of similar materials in the MatWeb database for the category "Polystyrene + Polyphenylene Ether, Glass Filler". Each property range of values reported is minimum and .. |
|||
Modulus of Elasticity | 3.80 GPa | 551 ksi | |
Lehmann & Voss LUVOCOM® 1106-7940/GY Polyether imide, unreinforced, laser markable Applications: High continuous use and heat distortion temperature. Non flammable.Dynamic stressed parts at high movement velocity.High dimensionally stable precision parts.Information provided by Le.. |