Lanxess Pocan® BFN 4231 000000 PBT, 25% Glass Fiber

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant
Manufacturer Lanxess
Trade Name Pocan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Pocan® BFN 4231 000000 PBT, 25% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PBT, 25% glass fibers, injection molding, halogen free flame retardantInformation provided by LANXESS.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Melt Flow 60.8 g/10 min

@Load 5.00 kg,
Temperature 260 °C
60.8 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ISO 1133-1
Mechanical Properties Metric English Comments
Tensile Strength at Break 100 MPa
14500 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 2.2 %
2.2 %
5 mm/min; ISO 527-1,-2
Tensile Modulus 10.5 GPa
1520 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 165 MPa
23900 psi
2 mm/min; ISO 178-A
Flexural Modulus 10.0 GPa
1450 ksi
2 mm/min; ISO 178-A
Izod Impact, Unnotched (ISO) 33.0 kJ/m²

@Temperature -30.0 °C
15.7 ft-lb/in²

@Temperature -22.0 °F
ISO 180-1U
36.0 kJ/m²

@Temperature 23.0 °C
17.1 ft-lb/in²

@Temperature 73.4 °F
ISO 180-1U
Charpy Impact Unnotched 3.50 J/cm²

@Temperature -30.0 °C
16.7 ft-lb/in²

@Temperature -22.0 °F
ISO 179-1eU
4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
16.7 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Melting Point 220 °C
428 °F
10 °C/min; ISO 11357-1,-3
Deflection Temperature at 0.46 MPa (66 psi) 224 °C
435 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ISO 75-1,-2
Vicat Softening Point 206 °C
403 °F
50 N; 120 °C/h; ISO 306
Flammability, UL94 V-0

@Thickness 0.400 mm
V-0

@Thickness 0.0157 in
V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
5VA

@Thickness 1.50 mm
5VA

@Thickness 0.0591 in
1.6 mm
Oxygen Index 43.7 %
43.7 %
Method A; ISO 4589-2
Glow Wire Test 775 °C

@Thickness 0.750 mm
1430 °F

@Thickness 0.0295 in
GWIT; IEC 60695-2-13
825 °C

@Thickness 1.50 mm
1520 °F

@Thickness 0.0591 in
GWIT; IEC 60695-2-13
850 °C

@Thickness 0.400 mm
1560 °F

@Thickness 0.0157 in
GWIT; IEC 60695-2-13
850 °C

@Thickness 3.00 mm
1560 °F

@Thickness 0.118 in
GWIT; IEC 60695-2-13
960 °C

@Thickness 0.400 mm
1760 °F

@Thickness 0.0157 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 0.750 mm
1760 °F

@Thickness 0.0295 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
GWFI; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
GWFI; IEC 60695-2-12
Shrinkage 0.100 %

@Temperature 120 °C,
Time 14400 sec
0.100 %

@Temperature 248 °F,
Time 4.00 hour
post-shrinkage, 60x60x2; ISO 294-4
0.100 %

@Temperature 120 °C,
Time 14400 sec
0.100 %

@Temperature 248 °F,
Time 4.00 hour
post-shrinkage, transverse, 60x60x2; ISO 294-4
Electrical Properties Metric English Comments
Volume Resistivity 2.30e+16 ohm-cm
2.30e+16 ohm-cm
IEC 60093
Surface Resistance 2.00e+16 ohm
2.00e+16 ohm
IEC 60093
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243-1
Comparative Tracking Index >= 600 V
>= 600 V
Solution A; UL 746A
Processing Properties Metric English Comments
Melt Temperature 260 °C
500 °F
Injection molding; ISO 294
Mold Temperature 80.0 °C
176 °F
Injection molding; ISO 294
Dry Time 4.00 - 8.00 hour

@Temperature 120 °C
4.00 - 8.00 hour

@Temperature 248 °F
Moisture Content 0.020 %
0.020 %
Karl Fischer test