Lanxess Durethan® BC 550 Z DUSXBL 900116 Nylon 6, Impact Modified

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BC 550 Z DUSXBL 900116 Nylon 6, Impact Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, non-reinforced, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.015 cm/cm
0.015 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0020 cm/cm
0.0020 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.015 cm/cm
0.015 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 50.0 MPa
7250 psi
d.a.m.; ISO 527-1, -2; 50 mm/min
Elongation at Break 140 %
140 %
d.a.m.; ISO 527-1, -2; 50 mm/min
Elongation at Yield 4.0 %
4.0 %
d.a.m.; ISO 527-1, -2; 50 mm/min
Tensile Modulus 2.00 GPa
290 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 21.0 MPa

@Strain 9.00 %
 3050 psi

@Strain 9.00 %
 cond., 2 mm/min; ISO 178-A
66.0 MPa

@Strain 6.00 %
 9570 psi

@Strain 6.00 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 14.0 MPa

@Strain 3.50 %
 2030 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
55.0 MPa

@Strain 3.50 %
 7980 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 0.470 GPa
68.2 ksi
cond., 2 mm/min; ISO 178-A
1.80 GPa
261 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) 25.0 kJ/m²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1A
85.0 kJ/m²

@Temperature 23.0 °C
 40.4 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 180-1A
105 kJ/m²

@Temperature 23.0 °C
 50.0 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 180-1A
Izod Impact, Unnotched (ISO) NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 d.a.m.; ISO 180-1U
NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 cond.; ISO 180-1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 d.a.m.; ISO 180-1U
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
Charpy Impact, Notched 2.50 J/cm²

@Temperature -30.0 °C
 11.9 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
13.0 J/cm²

@Temperature 23.0 °C
 61.9 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eA
Puncture Energy 65.0 J

@Load <=510 kg,
Temperature 23.0 °C
 47.9 ft-lb

@Load <=1120 lb,
Temperature 73.4 °F
 ISO 6603-2
67.0 J

@Load <=581 kg,
Temperature -30.0 °C
 49.4 ft-lb

@Load <=1280 lb,
Temperature -22.0 °F
 ISO 6603-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 140 µm/m-°C

@Temperature 23.0 - 55.0 °C
 77.8 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 130 µm/m-°C

@Temperature 23.0 - 55.0 °C
 72.2 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 219 °C
426 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 1.8 MPa (264 psi) 53.0 °C
127 °F
ISO 75-1, -2
Processing Properties Metric English Comments
Melt Temperature 230 - 280 °C
446 - 536 °F
260 °C
500 °F
for test specimens; ISO 294
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
80.0 °C
176 °F
for test specimens; ISO 294
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.00 - 0.060 %
0.00 - 0.060 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6-HI, BHR, 14-020