Polymer Property : Flexural Modulus = 68.2 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	0.470 GPa	68.2 ksi	method 1, Proc.B; ASTM D-790
Multibase Multi-Flex® TPE G 7680 NAT The burn rate is 1.2 in/min (30 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Flexural Modulus	0.470 GPa	68.2 ksi	conditioned, 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BC 550 DUSXBL 900116 Nylon 6 PA 6, non-reinforced, extrusion, Blastorm, impact modified, heat-ageing stabilizedInformation provided by LANXESS.
Flexural Modulus	0.470 GPa	68.2 ksi	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® BC 550 Z DUSXBL 900116 Nylon 6, Impact Modified PA 6, non-reinforced, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Flexural Modulus	0.470 GPa	68.2 ksi	cond., 2 mm/min; ISO 178-A
Lanxess DurethanÂ® TP 142-011 900116 Nylon 6 PA 6, non-reinforced, extrusion, blow molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Flexural Modulus	0.470 GPa	68.2 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics ULTEM SILTEM-STM1500 PEI (Europe-Africa-Middle East) SILTEM STM1500 is a flexible siloxane-polyetherimide copolymer for cable and wire coatings. RoHS compliant.
Flexural Modulus	0.470 GPa	68.2 ksi	ASTM D790
Elastomer Engineering Elastamide 300 Elastomer Modified RIM Nylon 6 22% crystallinity. Information supplied by Elastomer Engineering.
Flexural Modulus	0.470 GPa	68.2 ksi	ASTM D790
Covestro Baydur® 646 Polyurethane Structural Foam RIM, Density 25 pcf, MDI-based 2-Component Liquid System 0.25 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of..
Flexural Modulus	0.470 GPa	68.2 ksi	ASTM D790
Covestro Bayflex® 110-35 IMR Polyurethane Elastomeric RIM, 18% Mineral Filled, MDI-based 2-Component Liquid System Calcium Silicate filled. 0.15 in. thickness. IMR=Internal Mold Release RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Ba..
Flexural Modulus	0.470 - 2.07 GPa	68.2 - 300 ksi	Average value: 1.20 GPa Grade Count:11
Overview of materials for Thermoset Polyurethane, Elastomer, Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Thermoset Polyurethane, Elastomer, Glass Filled". Each property range of values reported is minimum and ..