LG Chemical LUPOY GN1006FM PC, Halogen Free, Flame Retardant, Transparency

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer LG Chemical
Trade Name LUPOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUPOY GN1006FM PC, Halogen Free, Flame Retardant, Transparency.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding, PC, Halogen Free Flame Retardant, TransparencyApplication: IT/OA, Electric & Electronic Housing and ComponentsCAS: 103598-77-2Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Maximum Moisture Content 0.020
0.020
Injection Molding
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 118
118
ASTM D785
Tensile Strength, Yield 61.8 MPa

@Thickness 3.20 mm
 8960 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break >= 100 %

@Thickness 3.20 mm
 >= 100 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Flexural Yield Strength 91.2 MPa

@Thickness 3.20 mm
 13200 psi

@Thickness 0.126 in
 10mm/min; ASTM D790
Flexural Modulus 2.26 GPa

@Thickness 3.20 mm
 327 ksi

@Thickness 0.126 in
 10mm/min; ASTM D790
Izod Impact, Notched >= 7.16 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 >= 13.4 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 130 °C

@Thickness 6.40 mm
 >= 266 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 141 °C

@Load 5.00 kg
 286 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 120 °C

@Thickness >=1.50 mm
 248 °F

@Thickness >=0.0591 in
120 °C

@Thickness >=2.00 mm
 248 °F

@Thickness >=0.0787 in
120 °C

@Thickness >=2.50 mm
 248 °F

@Thickness >=0.0984 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 110 °C

@Thickness >=1.50 mm
 230 °F

@Thickness >=0.0591 in
110 °C

@Thickness >=2.00 mm
 230 °F

@Thickness >=0.0787 in
110 °C

@Thickness >=2.50 mm
 230 °F

@Thickness >=0.0984 in
110 °C

@Thickness >=3.00 mm
 230 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 120 °C

@Thickness >=1.50 mm
 248 °F

@Thickness >=0.0591 in
120 °C

@Thickness >=2.00 mm
 248 °F

@Thickness >=0.0787 in
120 °C

@Thickness >=2.50 mm
 248 °F

@Thickness >=0.0984 in
120 °C

@Thickness >=3.00 mm
 248 °F

@Thickness >=0.118 in
Flammability, UL94 V-2

@Thickness >=1.50 mm
 V-2

@Thickness >=0.0591 in
V-1

@Thickness >=2.00 mm
 V-1

@Thickness >=0.0787 in
V-0

@Thickness >=2.50 mm
 V-0

@Thickness >=0.0984 in
V-0

@Thickness >=3.00 mm
 V-0

@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 2.00e+15 ohm-cm
2.00e+15 ohm-cm
ASTM D257
Arc Resistance 0.00 - 60 sec
0.00 - 60 sec
ASTM D495
Comparative Tracking Index 175 - 250 V
175 - 250 V
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 260 - 280 °C
500 - 536 °F
Injection Molding
Middle Barrel Temperature 280 - 300 °C
536 - 572 °F
Injection Molding
Front Barrel Temperature 300 - 320 °C
572 - 608 °F
Injection Molding
Nozzle Temperature 300 - 320 °C
572 - 608 °F
Injection Molding
Melt Temperature 300 - 320 °C
572 - 608 °F
Injection Molding
Mold Temperature 80.0 - 120 °C
176 - 248 °F
Injection Molding
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
Dry Time 3.00 - 5.00 hour
3.00 - 5.00 hour
Injection Molding
Back Pressure 0.981 - 3.92 MPa
142 - 569 psi
Injection Molding
Screw Speed 40 - 70 rpm
40 - 70 rpm
Injection Molding