Polymer Property : Drying Temperature = 120 °C Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Processing Properties Metric English Comments
Drying Temperature 100 - 120 °C
212 - 248 °F
Celanese Hostaform® C 9021 M POM, Tribological  (Unverified Data**)
Chemical abbreviation according to ISO 1043-1: POMInjection molding type like C 9021, with molybdenum disulphide modifiedInformation provided by Celanese
Drying Temperature 100 - 120 °C
212 - 248 °F
Celanese Hostaform® C 9021 TF5 POM, Tribological  (Unverified Data**)
Hostaform® C 9021 TF5 is a standard flow low level polytetraflouroethylene filled (PTFE) product designed for use in wear applications against plastics, metal, glass or ceramic mating surfaces whe..
Drying Temperature 70.0 - 120 °C
158 - 248 °F
Average value: 83.7 °C Grade Count:18
Overview of materials for Nylon 6, 20% Mineral Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 20% Mineral Filled". Specific grades with primary filler content between 15% and 24% are includ..
Drying Temperature 110 - 120 °C

@Time 10800 - 14400 sec
230 - 248 °F

@Time 3.00 - 4.00 hour
Pre-dry
Kingfa JH720 G30 30% Glass Fiber Reinforced PC
Features:High mechanical strengthGood size stabilityLow tendency to warpGood surfaceSuitable for exact moldingApplications:Imaging equipment shellOA body frameElectrical equipmentComputer plug parts..
Drying Temperature 100 - 120 °C
212 - 248 °F
LG Chemical LUMAX GP-5200 General Purpose PBT, 20 % Polymer Alloy
LUMAX resins are a family of thermoplastic blends of polybutyleneterephthalate(PBT) and styrenic resins that combine the most desirable properties of both resins and fillers. They offer high heat r..
Drying Temperature 100 - 120 °C
212 - 248 °F
LG Chemical LUMAX HF-5008 High Flow PBT, Dimensional Stability
LUMAX resins are a family of thermoplastic blends of polybutyleneterephthalate(PBT) and styrenic resins that combine the most desirable properties of both resins and fillers. They offer high heat r..
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
LG Chemical Lupox® GP1000SB PBT
Description: Injection Molding, PBT, Anti-HydrolysisApplication: IT/OA, Automotive (Connector)CAS No. 24968-12-5Information provided by LG Chemical
Drying Temperature 100 - 120 °C
212 - 248 °F
LG Chemical LUPOY GP-2400 General Purpose Modified PC, 40% Glass Fiber Reinforced, High Strength
Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive..
Drying Temperature 100 - 120 °C
212 - 248 °F
Injection Molding
LG Chemical LUPOY SC2302 PC+GF30%, High Impact
Description: Injection Molding, PC+GF30%, Good Toughness, Good Impact, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical
Drying Temperature 110 - 120 °C

@Time 10800 - 14400 sec
230 - 248 °F

@Time 3.00 - 4.00 hour
Pre-dry
Kingfa PC-WT01 Weather Resistance PC
Features:Excellent balance propertiesGood weather resistanceHigh impact strengthGood electro-plating propertiesGood processing propertiesApplications:Injection moldingAutomobile instrument panelElec..
Drying Temperature 100 - 120 °C

@Time 10800 sec
212 - 248 °F

@Time 3.00 hour
LATI Latilub 75/4-15ST G/30 PBT, 30% Glass Fiber Reinforced, Silicone/PTFE Filled
Self-lubricating product based on Polybutylene Terephthalate (PBT). Silicone / PTFE. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation pr..
Drying Temperature 110 - 120 °C
230 - 248 °F
Predrying Temperature
Tisan TISESTER® 30% Glass Fiber Reinforced and heat Stabilized Polybutylene Terephthalate
TISESTER has a wide area of application in automotive, electric/electronics and durable goods industries. General Specifications include: Excellent surface appearanceHigh corrosion and abrasion resi..
Drying Temperature 110 - 120 °C
230 - 248 °F
Predrying Temperature
Tisan TISESTER® UNR Polybutylene Terephthalate
TISESTER has a wide area of application in automotive, electric/electronics and durable goods industries. General Specifications include: Excellent surface appearanceHigh corrosion and abrasion resi..
Drying Temperature 100 - 120 °C
212 - 248 °F
Eurotec® Tecoform® PO20 NL RT POM, PTFE modified, natural
Information provided by Eurotec®
Drying Temperature 100 - 120 °C
212 - 248 °F
Eurotec® Tecoform® PO30 GB30 NL HS POM, 30% glass bead reinforced, heat stabilized, natural
Information provided by Eurotec®
Drying Temperature 100 - 120 °C
212 - 248 °F
Eurotec® Tecoform® PO20 AR10 NL HS POM, 10% aramid fiber reinforced, heat stabilized, natural
Information provided by Eurotec®
Drying Temperature 100 - 120 °C
212 - 248 °F
Celanese Hostaform® S 27063 XAP2® POM
Description: Easy flowing elastomer-containing injection molding type based on HOSTAFORM C 27021; with higher impact strength and reduced emissions. Burning rate ISO 3795 and FMVSS 302 < 100 mm/min ..
Drying Temperature 100 - 120 °C
212 - 248 °F
Celanese Hostaform® S 27242 XAP2 ™ POM, Impact Modified
Easy flow, impact modified injection molding grade, with good low temperature impact strength and good weld line strength and reduced emissions. Emission according to VDA 275 < 5 mg/kgInformation pr..
Drying Temperature 110 - 120 °C
230 - 248 °F
Celanese FORTRON FX4330T7 PPS, 30% Impact Modified
FX4330T7 is a 30% glass-fiber reinforced, impact modified injection molding grade offering high flow. Recommended processing conditions are identical to standard filled grades.YesInformation provid..
Drying Temperature 100 - 120 °C
212 - 248 °F
Celanese Hostaform® XGC25-LW01 POM, 25% Glass Reinforced
Hostaform« XGC25-LW01 is an injection molding grade reinforced with approx. 25% glass fibers and tribological modification for sliding applications requiring low friction and wear.Information provi..
Drying Temperature 100 - 120 °C
212 - 248 °F
Celanese Hostaform® C 9021 M XAP2® POM
Description: Injection molding type, modified with molybdenum disulphide; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to ther..
Drying Temperature 100 - 120 °C
212 - 248 °F
Celanese Hostaform® S 27064 XAP2® POM, Impact Modified
Description: Easy flowing, elastomer-containing injection molding type based on HOSTAFORM C 27021 with high toughness and reduced emissionsHB. Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for mo..
Drying Temperature 80.0 - 120 °C
176 - 248 °F
Average value: 114 °C Grade Count:19
Overview of materials for Polyvinyl Dichloride (PVDC)
This property data is a summary of similar materials in the MatWeb database for the category "Polyvinyl Dichloride (PVDC)". Each property range of values reported is minimum and maximum values of ap..
Drying Temperature 100 - 120 °C
212 - 248 °F
Celanese Hostaform® C 9021 TF XAP² ™ POM, Tribological  (Unverified Data**)
Chemical abbreviation according to ISO 1043-1: POMTribological, low EmissionInformation provided by Celanese
Drying Temperature 80.0 - 120 °C
176 - 248 °F
Celanese Hostaform® LX90GC15 POM, 15% Specialty  (Unverified Data**)
Preliminary Data Sheetfiber glass coupled grade with molded in metallic appearanceInformation provided by Celanese
Drying Temperature 110 - 120 °C
230 - 248 °F
Celanese FORTRON 205 PPS  (Unverified Data**)
0205 is an easy flowing unfilled grade. It demonstrates excellent chemical resistance and thermal stability. Intended for compounding with various fillers. Available standard in pellet (0205P4) and ..
Drying Temperature 80.0 - 120 °C
176 - 248 °F
BASF Ultradur® B 4300 K4 20% Glass Bead Filled PBT
Description: Is a PBT + ASA, Injection-molding grades containing 20% of glass beads for industrial parts with low warpage.Applications: Precision parts for optical instruments, fuel tank sensor unit..
Drying Temperature 110 - 120 °C
230 - 248 °F
Celanese FORTRON 320 PPS, Unfilled
0320 exhibits a high melt strength for extrusion processes. The material demonstrates excellent heat and chemical resistance. The intended use of this product is for extruding monofilament/fibers, r..
Drying Temperature 110 - 120 °C
230 - 248 °F
Celanese FORTRON 203 PPS  (Unverified Data**)
A very easy flowing unfilled grade. This grade demonstrates excellent chemical resistance and thermal stability. Intended for extrusion applications that do not require high melt strength and for c..
Drying Temperature 100 - 120 °C
212 - 248 °F
Celanese Hostaform® S 27064 POM, Impact Modified
Chemical abbreviation according to ISO 1043-1: POM-HIInformation provided by Celanese