LG Chemical LUMID GP2200A(W) PA6+GF20%, General Purpose

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled
Manufacturer LG Chemical
Trade Name LUMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LUMID GP2200A(W) PA6+GF20%, General Purpose.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, PA6+MF23%, High ImpactPA6+GF20%, General PurposeApplication: HMID, SLMP B, HolderCAS No. 32131-17-2 and 65997-17-3Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Water Absorption 1.2 %
1.2 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0060 - 0.010 cm/cm

@Thickness 3.20 mm
 0.0060 - 0.010 in/in

@Thickness 0.126 in
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength, Yield 147 MPa

@Thickness 3.20 mm
 21300 psi

@Thickness 0.126 in
 5mm/min; ASTM D638
Elongation at Break 4.0 %

@Thickness 3.20 mm
 4.0 %

@Thickness 0.126 in
 5mm/min; ASTM D638
Flexural Yield Strength 216 MPa

@Thickness 6.40 mm
 31300 psi

@Thickness 0.252 in
 3mm/min; ASTM D790
Flexural Modulus 6.67 GPa

@Thickness 6.40 mm
 967 ksi

@Thickness 0.252 in
 3mm/min; ASTM D790
Izod Impact, Notched 0.883 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 1.65 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 45.0 µm/m-°C
25.0 µin/in-°F
ASTM D696
Melting Point 220 °C
428 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 205 °C

@Thickness 6.40 mm
 401 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness >=0.750 mm
 149 °F

@Thickness >=0.0295 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness >=0.750 mm
 149 °F

@Thickness >=0.0295 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness >=0.750 mm
 149 °F

@Thickness >=0.0295 in
Flammability, UL94 HB

@Thickness >=0.750 mm
 HB

@Thickness >=0.0295 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
 3.8

@Frequency 1.00e+6 Hz
 ASTM D150
Dielectric Strength 20.0 kV/mm

@Thickness 1.00 mm
 508 kV/in

@Thickness 0.0394 in
 ASTM D149
Arc Resistance 150 sec
150 sec
ASTM D495
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness >=0.750 mm
 15 - 30 sec

@Thickness >=0.0295 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.750 mm
 >= 120 arcs

@Thickness 0.0295 in
High Voltage Arc-Tracking Rate, HVTR 25.4 - 50.0 mm/min
1.00 - 1.97 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 235 - 255 °C
455 - 491 °F
Injection Molding
Middle Barrel Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Front Barrel Temperature 240 - 270 °C
464 - 518 °F
Injection Molding
Nozzle Temperature 250 - 280 °C
482 - 536 °F
Injection Molding
Melt Temperature 250 - 280 °C
482 - 536 °F
Injection Molding
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Injection Molding
Dry Time 4.00 - 5.00 hour
4.00 - 5.00 hour
Injection Molding