LATI Kelon® B FR H CET/30-V0 PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized

Category Polymer , Thermoplastic , Nylon , Nylon 6
Manufacturer LATI
Trade Name Kelon® B
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Kelon® B FR H CET/30-V0 PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Low thermal expansion coefficient. Very high dimensional stability. High stiffness.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.59 g/cc
0.0574 lb/in³
Linear Mold Shrinkage, Flow 0.0030 - 0.0055 cm/cm
0.0030 - 0.0055 in/in
Linear Mold Shrinkage, Transverse 0.0035 - 0.0060 cm/cm
0.0035 - 0.0060 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 20.0 MPa

@Temperature 150 °C
 2900 psi

@Temperature 302 °F
25.0 MPa

@Temperature 120 °C
 3630 psi

@Temperature 248 °F
30.0 MPa

@Temperature 90.0 °C
 4350 psi

@Temperature 194 °F
50.0 MPa

@Temperature 60.0 °C
 7250 psi

@Temperature 140 °F
65.0 MPa

@Temperature 23.0 °C
 9430 psi

@Temperature 73.4 °F
Elongation at Break 1.5 %

@Temperature 23.0 °C
 1.5 %

@Temperature 73.4 °F
2.3 %

@Temperature 60.0 °C
 2.3 %

@Temperature 140 °F
5.1 %

@Temperature 90.0 °C
 5.1 %

@Temperature 194 °F
10 %

@Temperature 120 °C
 10 %

@Temperature 248 °F
20 %

@Temperature 150 °C
 20 %

@Temperature 302 °F
Tensile Modulus 2.30 GPa

@Temperature 150 °C
 334 ksi

@Temperature 302 °F
2.60 GPa

@Temperature 120 °C
 377 ksi

@Temperature 248 °F
3.40 GPa

@Temperature 90.0 °C
 493 ksi

@Temperature 194 °F
6.50 GPa

@Temperature 60.0 °C
 943 ksi

@Temperature 140 °F
10.0 GPa

@Temperature 23.0 °C
 1450 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
1.50 J/cm²

@Temperature -20.0 °C
 7.14 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 0.200 J/cm²

@Temperature 23.0 °C
 0.952 ft-lb/in²

@Temperature 73.4 °F
0.200 J/cm²

@Temperature -20.0 °C
 0.952 ft-lb/in²

@Temperature -4.00 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 115 °C
239 °F
Deflection Temperature at 0.46 MPa (66 psi) 205 °C
401 °F
Deflection Temperature at 1.8 MPa (264 psi) 155 °C
311 °F
Vicat Softening Point 195 °C

@Load 5.00 kg
 383 °F

@Load 11.0 lb
Flammability, UL94 V-2

@Thickness 0.750 mm
 V-2

@Thickness 0.0295 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 28 %
28 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 450 V
450 V
A solution
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa