- HOME
- POLYMER SEARCH
- Polymer Property : Tensile Strength at Break = 3630 psi
Polymer Property : Tensile Strength at Break = 3630 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
|
| LATI Kelon® B H CER/30 PA 6, 30% Mineral Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. Very high dimensional stability. Good elongation.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North Ame.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 150 °C |
3630 psi @Temperature 302 °F |
|
| LATI Larpeek 10 PEEK Polyetheretherketone (PEEK). Unfilled. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe;.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 90.0 °C |
3630 psi @Temperature 194 °F |
|
| LATI Latamid 6 H2 G/20-V0 PA 6, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE and antimony trioxide free. Availability: Africa & Middle East; Asia .. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 23.0 °C |
3630 psi @Temperature 73.4 °F |
|
| LATI Latene® 7H2W TR/40 PP Homopolymer, Mineral Reinforced, Heat Stabilized Polypropylene homopolymer (PPh) based compound. Heat stabilized. Metal stabilized. Mineral filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation pr.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 23.0 °C |
3630 psi @Temperature 73.4 °F |
|
| LATI Latene® 7H2W T-V0E PP Homopolymer, Mineral Reinforced, Heat Stabilized, Flame Retardant Polypropylene homopolymer (PPh) based compound. Heat stabilized. Metal stabilized. Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
|
| LATI Kelon® B FR H CET/30-V0 PA 6, Mineral Reinforced, Flame Retardant, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Low thermal expansion coefficient. Very high dimensional stab.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
|
| LATI Kelon® B H CET/30 PA 6, 30% Mineral Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Mineral filler. Very high dimensional stability. Good elongationAvailability: Africa & Middle East; Asia Pacific; Europe; Latin America; North Amer.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 150 °C |
3630 psi @Temperature 302 °F |
|
| LATI Kelon® B H CETG/300 PA 6, Glass/Mineral Reinforced, Heat Stabilized Polyamide 6 (PA6) based compound. Heat stabilized. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati I.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
|
| LATI Laril 13 G/20 PPOm, 20% Glass Fiber Reinforced Modified Polyphenylene Oxide (PPOm) based compound. Glass fibers. Low thermal expansion coefficient. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; .. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 60.0 °C |
3630 psi @Temperature 140 °F |
|
| LATI Latamid 6 H2PX-V0 PA 6, Heat Stabilized, Flame Retardant Polyamide 6 (PA6) based compound. Heat stabilized. Toughened. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin Am.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
|
| LATI Latamid 6 S/30 PA 6, 30% Glass Bead Reinforced Polyamide 6 (PA6) based compound. Glass beads. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Indu.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 150 °C |
3630 psi @Temperature 302 °F |
|
| LATI Latamid 66 S/30 PA 66, 30% Glass Bead Reinforced Polyamide 66 (PA66) based compound. Glass beads. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 60.0 °C |
3630 psi @Temperature 140 °F |
|
| LATI Latan 13 S/30 POM, 30% Glass Bead Reinforced Polyoxymethylene (POM) based compound. Glass beads. Medium viscosity. High dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation pro.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 90.0 °C |
3630 psi @Temperature 194 °F |
|
| LATI Latene® AG7H K/30 PP Homopolymer, 30% Carbon Fiber Reinforced, Heat Stabilized Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Carbon fiber. Good thermal properties.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; Nort.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 23.0 °C |
3630 psi @Temperature 73.4 °F |
|
| LATI Latene® AG9H MI/40 PP Homopolymer, 40% Mica Reinforced, Heat Stabilized Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Mica filler.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provi.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 60.0 °C |
3630 psi @Temperature 140 °F |
|
| LATI Later 4-V0HF1 PBT, Flame Retardant Polybutylene Terephthalate (PBT) based compound. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin Americ.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 90.0 °C |
3630 psi @Temperature 194 °F |
|
| LATI Latilon 28D-V0 PC, Flame Retardant Polycarbonate (PC) based compound. UL94 V-0 classified, brominated and chlorinated halogens-based flame retardants free. Low smoke density and low toxicity index. Very high dimensional stability. Ve.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 60.0 °C |
3630 psi @Temperature 140 °F |
|
| LATI Latilon 30D G/10-V0 PC, 10% Glass Fiber Reinforced, Flame Retardant Polycarbonate (PC) based compound. Glass fibers. UL94 V-0 classified, brominated and chlorinated halogens-based flame retardants free. Low smoke density and low toxicity index. High dimensional stab.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 0.000 °C |
3630 psi @Temperature 32.0 °F |
ASTM D638 |
| Borealis Borstar® HE6081 Black Track Resistant HD Polyethylene Based Compound for Jacketing of Fiber Optical Cable Borstar HE6081 is based on high-density polyethylene and has a specially designed additive package to give excellent track resistance. It is also well protected against UV degradation in order to e.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature -30.0 °C |
3630 psi @Temperature -22.0 °F |
ASTM D638 |
| Borealis Borstar® HE6081 Black Track Resistant HD Polyethylene Based Compound for Jacketing of Fiber Optical Cable Borstar HE6081 is based on high-density polyethylene and has a specially designed additive package to give excellent track resistance. It is also well protected against UV degradation in order to e.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 90.0 °C |
3630 psi @Temperature 194 °F |
|
| LATI Lastil G/30 SAN, 30% Glass Fiber Reinforced Styrene-Acrylonitrile copolymer (SAN) based compound. Glass fibers. High dimensional stability. High stiffness.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaI.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 120 °C |
3630 psi @Temperature 248 °F |
|
| LATI Kelon® A FR H2 CET/35-V2 PA 66, 35% Mineral Reinforced, Flame Retardant, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Mineral filler. UL94 V-2 classified, with brominated flame retardants, PBB/PBDE free.Availability: Africa & Middle East; Asia Pacific; Europe; La.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 150 °C |
3630 psi @Temperature 302 °F |
|
| LATI Kelon® A H CEG/40 PA 66, Glass/Mineral Reinforced, Heat Stabilized Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers / Mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati.. |
|||
| Tensile Strength at Break | 25.0 MPa @Temperature 275 °C |
3630 psi @Temperature 527 °F |
ISO 527 |
| Victrex® PEEK 450GL15 Polyetheretherketone, 15% Glass Fibre Reinforced Product Description:High performance thermoplastic material, 15% glass fibre reinforced Polyetheretherketone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, F.. |
|||