- Ineos Nova Styrosun® 6600 Weather Resistant High Impact Styrenic Polymer
Ineos Nova Styrosun® 6600 Weather Resistant High Impact Styrenic Polymer
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Nova |
| Trade Name | Styrosun® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Nova Styrosun® 6600 Weather Resistant High Impact Styrenic Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Outdoor weatherablePhysical property retention after UV exposurePaintable and printableExcellent toughness Can be injection molded or co-extruded Easy to process, no drying required Applications: Building/construction Outdoor signsIrrigation/sprinkler systemsGardening and yard accessoriesOutdoor trays, containersInformation provided by Nova ChemicalsINEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets.Â
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 2.1 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.1 g/10 min @Load 11.0 lb, Temperature 392 °F |
old Condition G; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Tensile Modulus | 2.28 GPa | 331 ksi | ASTM D638 |
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 2.50 J/cm | 4.68 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | annealed; ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 182 - 204 °C | 360 - 399 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 399 - 441 °F | |
| Front Barrel Temperature | 216 - 238 °C | 421 - 460 °F | |
| Melt Temperature | 221 - 243 °C | 430 - 469 °F | |
| Back Pressure | 0.345 MPa | 50.0 psi |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 1.0 PHR MBT
- LG Chemical Lupox® LW5300M PBT+PC+MF30%
- Lotte Chemical Titan TITANLENE® LDF260YZ Low density polyethylene
- SABIC Innovative Plastics Noryl PC180X PPE+PS
- Hexcel® HexPly® F515 Epoxy Resin
- CTC X-PRO TF 1120 HP Polypropylene Homopolymer, 20% Talc Filled
- Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (1.5 mm Molded Thickness)
- Braskem TI4015F2 Impact Copolymer Polypropylene
- ATI Allvac® 55, Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal
- A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene
Copyright © lookpolymers.com All Rights Reserved