CTC X-PRO TF 1120 HP Polypropylene Homopolymer, 20% Talc Filled

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler
Manufacturer CTC (Composite Technologies)
Trade Name X-PRO
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CTC X-PRO TF 1120 HP Polypropylene Homopolymer, 20% Talc Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
X-PRO TF 1120 HP is a 20% talc reinforced polypropylene homopolymer, heat stabilized, and made of 98% recycled content. It has applications in: automotive under hood, IP components, fan and lighting shrouds, HVAC components, lawn & garden, pipe fittings, and appliances.Data provided by Composite Technologies (CTC).
Physical Properties Metric English Comments
Melt Flow 20 g/10 min
20 g/10 min
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 31.0 MPa
4500 psi
ISO 527-1/2
Flexural Modulus 2.50 GPa
363 ksi
0.05 in/min; ISO 178
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
Low Temp; ISO 180/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 118 °C
245 °F
ASTM-D648
Deflection Temperature at 1.8 MPa (264 psi) 65.6 °C
150 °F
ASTM-D648
Processing Properties Metric English Comments
Rear Barrel Temperature 204 - 216 °C
400 - 420 °F
Middle Barrel Temperature 216 - 227 °C
420 - 440 °F
Front Barrel Temperature 227 - 238 °C
440 - 460 °F
Melt Temperature 227 - 238 °C
440 - 460 °F
Mold Temperature 26.7 - 60.0 °C
80.0 - 140 °F
Back Pressure 0.689 - 1.03 MPa
100 - 150 psi
Clamp Pressure 27.6 - 34.5 MPa
4000 - 5000 psi
Descriptive Properties Value Comments
Boost Pressure (psi) 750-1500
Hold Pressure 50 - 75% of Boost
Screw Speed Fast