Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (1.5 mm Molded Thickness)

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Azdel
Trade Name SuperLite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (1.5 mm Molded Thickness).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AZDEL SuperLite® SL550900-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applications. Typically used in non-structural applications where a very high strength to weight ratio is required, such as:Automotive headlinersDoor panelsPackage shelvesOther interior trimPhysical properties apply only to bare SuperLite sheet and do not include surface films or scrim. Mechanical properties measured on flat plaques.Draw ratio is defined as the ratio of the maximum depth of the mold to the minimum distance across the open face of the mold at any given location and is measured on flat plaques.Information provided by Azdel.
Physical Properties Metric English Comments
Specific Gravity 0.700 g/cc
0.700 g/cc
ASTM D3574
Filler Content 55 %
55 %
ASTM D5630
Thickness 5300 - 5800 microns
209 - 228 mil
Typical free lofted thickness after heating
Linear Mold Shrinkage <= 0.00020 cm/cm
<= 0.00020 in/in
Typical, molds cut to zero
Mechanical Properties Metric English Comments
Tensile Strength at Break 42.0 MPa
6090 psi
ASTM D638
Tensile Modulus 4.60 GPa
667 ksi
ASTM D638
Flexural Strength 18.5 MPa
2680 psi
SAE J949
Flexural Modulus 2.70 GPa
392 ksi
SAE J949
Impact 650
650
Multi-axial in Newtons, at 23°C, at max. load, measured on flat plaques; ASTM D3763
Impact Test 2.20 J

@Temperature 23.0 °C
1.62 ft-lb

@Temperature 73.4 °F
Multi-axial, at max. load; ASTM D3763
4.80 J

@Temperature 23.0 °C
3.54 ft-lb

@Temperature 73.4 °F
Multi-axial, at failure, measured on flat plaques; ASTM D3763
Descriptive Properties Value Comments
Available Colors Natural and Charcoal
Draw Ratio Max 1.5:1