Material Notes:
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming and welding characteristics. Applications include a variety of fabricated components in municipal, industrial, hazardous, and nuclear waste heat recovery systems. Also suitable for utility boilers, sulfur plants, high-temperature furnaces, kilns, calciners, resource recovery units, cement kilns, pulp and paper recovery boilers, coal gasification systems, and fluidized-bed-combustion systems.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.08 g/cc
0.292 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 767 MPa
111000 psi
30.0 MPa

@Temperature 1204 °C
 4350 psi

@Temperature 2199 °F
41.0 MPa

@Temperature 1149.0 °C
 5950 psi

@Temperature 2100.2 °F
74.0 MPa

@Temperature 1093 °C
 10700 psi

@Temperature 1999 °F
140 MPa

@Temperature 982 °C
 20300 psi

@Temperature 1800 °F
264 MPa

@Temperature 871 °C
 38300 psi

@Temperature 1600 °F
428 MPa

@Temperature 760 °C
 62100 psi

@Temperature 1400 °F
523 MPa

@Temperature 649 °C
 75900 psi

@Temperature 1200 °F
564 MPa

@Temperature 538 °C
 81800 psi

@Temperature 1000 °F
605 MPa

@Temperature 427 °C
 87700 psi

@Temperature 801 °F
634 MPa

@Temperature 316 °C
 92000 psi

@Temperature 601 °F
675 MPa

@Temperature 204 °C
 97900 psi

@Temperature 399 °F
717 MPa

@Temperature 93.0 °C
 104000 psi

@Temperature 199 °F
Tensile Strength, Yield 314 MPa

@Strain 0.200 %
 45500 psi

@Strain 0.200 %
11.0 MPa

@Strain 0.200 %,
Temperature 1204 °C
 1600 psi

@Strain 0.200 %,
Temperature 2199 °F
16.0 MPa

@Strain 0.200 %,
Temperature 1149 °C
 2320 psi

@Strain 0.200 %,
Temperature 2100 °F
34.0 MPa

@Strain 0.200 %,
Temperature 1093 °C
 4930 psi

@Strain 0.200 %,
Temperature 1999 °F
74.0 MPa

@Strain 0.200 %,
Temperature 982 °C
 10700 psi

@Strain 0.200 %,
Temperature 1800 °F
152 MPa

@Strain 0.200 %,
Temperature 871 °C
 22000 psi

@Strain 0.200 %,
Temperature 1600 °F
170 MPa

@Strain 0.200 %,
Temperature 760 °C
 24700 psi

@Strain 0.200 %,
Temperature 1400 °F
176 MPa

@Strain 0.200 %,
Temperature 538 °C
 25500 psi

@Strain 0.200 %,
Temperature 1000 °F
177 MPa

@Strain 0.200 %,
Temperature 649 °C
 25700 psi

@Strain 0.200 %,
Temperature 1200 °F
179 MPa

@Strain 0.200 %,
Temperature 427 °C
 26000 psi

@Strain 0.200 %,
Temperature 801 °F
190 MPa

@Strain 0.200 %,
Temperature 316 °C
 27600 psi

@Strain 0.200 %,
Temperature 601 °F
233 MPa

@Strain 0.200 %,
Temperature 204 °C
 33800 psi

@Strain 0.200 %,
Temperature 399 °F
279 MPa

@Strain 0.200 %,
Temperature 93.0 °C
 40500 psi

@Strain 0.200 %,
Temperature 199 °F
Elongation at Break 68 %
68 %
in 34.0 mm
69 %

@Temperature 93.0 °C
 69 %

@Temperature 199 °F
 in 34.0 mm
70 %

@Temperature 649 °C
 70 %

@Temperature 1200 °F
 in 34.0 mm
71 %

@Temperature 204 °C
 71 %

@Temperature 399 °F
 in 34.0 mm
73 %

@Temperature 760 °C
 73 %

@Temperature 1400 °F
 in 34.0 mm
74 %

@Temperature 316 °C
 74 %

@Temperature 601 °F
 in 34.0 mm
76 %

@Temperature 427 °C
 76 %

@Temperature 801 °F
 in 34.0 mm
76 %

@Temperature 538 °C
 76 %

@Temperature 1000 °F
 in 34.0 mm
85 %

@Temperature 871 °C
 85 %

@Temperature 1600 °F
 in 34.0 mm
88 %

@Temperature 1093 °C
 88 %

@Temperature 1999 °F
 in 34.0 mm
90 %

@Temperature 982 °C
 90 %

@Temperature 1800 °F
 in 34.0 mm
110 %

@Temperature 1204 °C
 110 %

@Temperature 2199 °F
 in 34.0 mm
113 %

@Temperature 1149.0 °C
 113 %

@Temperature 2100.2 °F
 in 34.0 mm
Reduction of Area 73 %
73 %
64 %

@Temperature 760 °C
 64 %

@Temperature 1400 °F
67 %

@Temperature 649 °C
 67 %

@Temperature 1200 °F
68 %

@Temperature 427 °C
 68 %

@Temperature 801 °F
69 %

@Temperature 538 °C
 69 %

@Temperature 1000 °F
70 %

@Temperature 316 °C
 70 %

@Temperature 601 °F
74 %

@Temperature 93.0 °C
 74 %

@Temperature 199 °F
74 %

@Temperature 204 °C
 74 %

@Temperature 399 °F
84 %

@Temperature 871 °C
 84 %

@Temperature 1600 °F
94 %

@Temperature 1204 °C
 94 %

@Temperature 2199 °F
94 %

@Temperature 1149.0 °C
 94 %

@Temperature 2100.2 °F
98 %

@Temperature 982 °C
 98 %

@Temperature 1800 °F
98 %

@Temperature 1093 °C
 98 %

@Temperature 1999 °F
Modulus of Elasticity 211 GPa
30600 ksi
137 GPa

@Temperature 980 °C
 19900 ksi

@Temperature 1800 °F
145 GPa

@Temperature 925 °C
 21000 ksi

@Temperature 1700 °F
150 GPa

@Temperature 870 °C
 21800 ksi

@Temperature 1600 °F
154 GPa

@Temperature 815 °C
 22300 ksi

@Temperature 1500 °F
158 GPa

@Temperature 760 °C
 22900 ksi

@Temperature 1400 °F
163 GPa

@Temperature 705 °C
 23600 ksi

@Temperature 1300 °F
168 GPa

@Temperature 650 °C
 24400 ksi

@Temperature 1200 °F
173 GPa

@Temperature 595 °C
 25100 ksi

@Temperature 1100 °F
177 GPa

@Temperature 540 °C
 25700 ksi

@Temperature 1000 °F
180 GPa

@Temperature 480 °C
 26100 ksi

@Temperature 896 °F
183 GPa

@Temperature 425 °C
 26500 ksi

@Temperature 797 °F
187 GPa

@Temperature 370 °C
 27100 ksi

@Temperature 698 °F
192 GPa

@Temperature 315 °C
 27800 ksi

@Temperature 599 °F
197 GPa

@Temperature 260 °C
 28600 ksi

@Temperature 500 °F
201 GPa

@Temperature 205 °C
 29200 ksi

@Temperature 401 °F
204 GPa

@Temperature 150 °C
 29600 ksi

@Temperature 302 °F
208 GPa

@Temperature 90.0 °C
 30200 ksi

@Temperature 194 °F
210 GPa

@Temperature 40.0 °C
 30500 ksi

@Temperature 104 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.0001112 ohm-cm
0.0001112 ohm-cm
0.0001231 ohm-cm

@Temperature 700 °C
 0.0001231 ohm-cm

@Temperature 1290 °F
0.0001238 ohm-cm

@Temperature 800 °C
 0.0001238 ohm-cm

@Temperature 1470 °F
0.0001245 ohm-cm

@Temperature 900 °C
 0.0001245 ohm-cm

@Temperature 1650 °F