- Polymer Property : Modulus of Elasticity = 27800 ksi
Polymer Property : Modulus of Elasticity = 27800 ksi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 192 GPa @Temperature 315 °C |
27800 ksi @Temperature 599 °F |
|
| Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 315 °C |
27800 ksi @Temperature 599 °F |
|
| Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 40% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 30% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Modulus of Elasticity | 192 GPa | 27800 ksi | |
| Carlson 926 Mo Austenitic Stainless Steel General DescriptionCarlson alloy 926 Mo is a “super-austenitic” 6% molybdenum stainless steel that provides excellent resistance to a variety of highly corrosive environments. This alloy performs.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 30% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 0.71 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 427 °C |
27800 ksi @Temperature 801 °F |
plate heat treated to 1177°C and rapid quenched |
| Haynes Hastelloy® G-30® alloy, 31.8 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| Modulus of Elasticity | 192 GPa | 27800 ksi | Young's Modulus |
| Ceramic Process Systems AlSiC-9, 63 vol% SiC Aluminum alloy A356.2 used. Hermeticity < 1x109 atm-cc/s He.CPS fabricates AlSiC by preparing an SiC preform which is subsequently infiltrated by molten aluminum metal. After infiltration, compone.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
| Modulus of Elasticity | 192 GPa @Temperature 300 °C |
27800 ksi @Temperature 572 °F |
|
| Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||