Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | X, Y direction; ASTM D638 |
Rogers Corporation RT/duroid® 6202 High Frequency Laminate Features:Low loss for excellent high frequency performanceTight dielectric constant and thickness controlExcellent electrical and mechanical propertiesExtremely low thermal coefficient of dielectric.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | X, Y direction; ASTM D638 |
Rogers Corporation RT/duroid® 6202PR High Frequency Laminate Features:Low loss for excellent high frequency performanceTight dielectric constant and thickness controlExcellent electrical and mechanical propertiesExtremely low thermal coefficient of dielectric.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO 527-2 |
NOVA Chemicals DYLARK® 378 Impact Grade Engineering Resin Features:High heat resistance Good chemical resistance High impact strength Excellent flow characteristicsApplications:Automotive interior trim applications Automotive consoles Structural HousingsIn.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO 527 |
LATI LASTIROL R-V0 Polystyrene (PS) (UL94 V-0)
(discontinued **) Lastirol thermoplastics are polystyrene (PS) products. The Lastirols feature excellent dimensional stability, good flowability, and can be molded without any particular problem. Glass fiber reinforc.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | DIN 53455 |
Ineos Nova S-4400 High Impact Compact Polystyrene
(discontinued **) Impact polystyrene which combines excellent flow characteristics with a good dimensional stability under heat and a high stiffness. This grade is designed for injection molding of technical parts o.. |
|||
Tensile Strength, Ultimate | 30.0 - 44.9 MPa | 4350 - 6510 psi | Average value: 41.3 MPa Grade Count:11 |
Overview of materials for PVC, High Impact This property data is a summary of similar materials in the MatWeb database for the category "PVC, High Impact". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
Tensile Strength, Ultimate | 30.0 - 50.0 MPa | 4350 - 7250 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 21508 PVDF Copolymer
(discontinued **) Key features of this grade: High Elongation, Wire & Cable, Plenum, Formulated. Recommended processing is extrusion. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® P.. |
|||
Tensile Strength, Ultimate | 30.0 - 215 MPa | 4350 - 31200 psi | Average value: 149 MPa Grade Count:581 |
Overview of materials for Nylon 66, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. .. |
|||
Tensile Strength, Ultimate | 30.0 - 145 MPa @Temperature 60.0 - 150 °C |
4350 - 21000 psi @Temperature 140 - 302 °F |
Average value: 78.6 MPa Grade Count:14 |
Overview of materials for Nylon 66, Glass Fiber Filled, Flame Retardant This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Fiber Filled, Flame Retardant". Each property range of values reported is minimum and ma.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | |
Kuraray HYBRAR® PH4 Polypropylene Blend Description: HYBRAR® is another in the series of new high performance thermoplastic rubbers developed by KURARAY using their unique isoprene technology. HYBRAR® is a special thermoplastic rubb.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | |
Momentive Performance Materials TSE3940 Gray Adhesive Sealant, Fast Cure Paste One-part totally non-corrosive alkoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: Flame retardant, no.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | |
Momentive Performance Materials TSE3941 White Adhesive Sealant, Fast Cure Paste One-part totally non-corrosive alkoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: Flame retardant, no.. |
|||
Tensile Strength, Ultimate | 30.0 MPa @Temperature 1205 °C |
4350 psi @Temperature 2201 °F |
|
Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh .. |
|||
Tensile Strength, Ultimate | 30.0 MPa @Temperature 22.0 °C |
4350 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® BMC 2910 Unsaturated Polyester UP BMC 2910 incorporates additives which enhance the integral performance of mouldings during and after fire, currently used to mould Boltcaps which are designed to provide protection to the bolted co.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO 527-1 |
Chengdu Polyster H5550 Thermoplastic Polyether-ester Elastomer (TPEE) Medium-low modulus molding and injection grade. Contains improved color- stable antioxidants. Good balance of low and high temperature properties. Applications requiring high original color retentio.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO 527-1 |
Chengdu Polyster H5550B Thermoplastic Polyether-ester Elastomer (TPEE) Low modulus molding and extrusion grade. Contains color-stable antioxidants. Good balance of low and high temperature properties. Excellent flex-fatigue resistance. Excellent creep resistance. CVJ b.. |
|||
Tensile Strength, Ultimate | 30.0 - 32.0 MPa | 4350 - 4640 psi | UV Postcure; ASTM D638M |
DSM Somos® 9120 The need for movable parts is a constant when it comes to prototyping. Being able to ensure the proper fit for parts within a component can save both time and money. Somos® 9120 creates semi-transp.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ISO R527 |
Arkema Group Orgalloy® LT 4060 Polyamide Alloy Polyamide Alloy, Flexible gradeTubes / Mandrels / Profiles / CablesInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ASTM D412 |
BASF Elastollan® 1175AW Polyether Type Polyurethane Elastomer Processed by extrusion or injection molding. Elastollan ® 1100 series products are FDA Sec. 177.2600 compliant. Elastollan 1100 series of products are polyether-based thermoplastic polyurethanes... |
|||
Tensile Strength, Ultimate | 30.0 - 80.0 MPa | 4350 - 11600 psi | |
Alliance BIF-17 Bonded (Composite) Magnetic Material |
|||
Tensile Strength, Ultimate | 30.0 - 80.0 MPa | 4350 - 11600 psi | |
Alliance BIF-19 Bonded (Composite) Magnetic Material |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | ASTM D638 |
A. Schulman ComAlloy Voloy® 110 Polypropylene, Mineral Reinforced, Flame Retardant, UL Data provided by the manufacturer, ComAlloy International Company.15% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 30.0 - 50.0 MPa | 4350 - 7250 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 20810 PVDF Copolymer
(discontinued **) Key features of this grade: Li Battery, Virgin. Recommended processing is solution. Available as powder & granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crysta.. |
|||
Tensile Strength, Ultimate | 30.0 - 170 MPa @Temperature -20.0 - 150 °C |
4350 - 24700 psi @Temperature -4.00 - 302 °F |
Average value: 104 MPa Grade Count:1 |
Overview of materials for Nylon 6, 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Tensile Strength, Ultimate | 30.0 MPa @Temperature 899 °C |
4350 psi @Temperature 1650 °F |
0.059" Coil |
AK Steel 15 Cr-Cb® ULTRA FORM® Ferritic Stainless steel AK Steel’s 15 Cr-Cb ULTRA FORM® is a low-carbon, low-nitrogen ferritic grade of stainless steel with an intermediate, 14.5% chromium content. Alloying additions of Ti, Cb, Si and Mn provide excell.. |
|||
Tensile Strength, Ultimate | 30.0 MPa | 4350 psi | DIN 53504 |
Lubrizol ESTANE® 54630 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 30.0 - 35.9 MPa | 4350 - 5210 psi | Average value: 33.9 MPa Grade Count:3 |
Overview of materials for Polypropylene, Sheet/Thermoforming Grade This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Sheet/Thermoforming Grade". Each property range of values reported is minimum and maximum.. |