- Polymer Property : Modulus of Elasticity = 150 GPa
Polymer Property : Modulus of Elasticity = 150 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, 40% cold reduction Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applic.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 870 °C |
21800 ksi @Temperature 1600 °F |
|
| Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 870 °C |
21800 ksi @Temperature 1600 °F |
|
| Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 870 °C |
21800 ksi @Temperature 1600 °F |
|
| Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F) Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an.. |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance C-5 Strontium Ferrite Ceramic Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance C-7B Strontium Ferrite Ceramic Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance C-8 Strontium Ferrite Ceramic Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance C-8H Strontium Ferrite Ceramic Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-30UH Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-35SH Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-38 Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-40M Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-42SH Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-45 Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance S-28B Samarium Cobalt Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance C-8B Strontium Ferrite Ceramic Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-30EZ Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 - 160 GPa | 21800 - 23200 ksi | |
| Alliance N-33H Neodymium Iron Boron Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | |
| Alliance S-28H Samarium Cobalt Magnetic Material |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, GMAW deposit weld metal Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 150 GPa | 21800 ksi | Filament in Tension |
| 3M Nextel™ 312 Industrial Ceramic Fiber Chemical composition above is wt%. Crystal phase is mullite + amorphous (or 100% amorphous). Filament diameter is 10-12 µm.3M Nextel fibers 312, 440, and 550 are designed for non-structural appli.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||
| Modulus of Elasticity | 150 GPa @Temperature 1000 °C |
21800 ksi @Temperature 1830 °F |
|
| Haynes 230® alloy, 50% cold reduction, 1177°C anneal for 5 minutes Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applicat.. |
|||