Polymer Property : Electrical Resistivity = 0.0001231 ohm-cm Product List

Electrical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Electrical Properties Metric English Comments
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-120® alloy, solution heat-treated
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-120® alloy, solution heat-treated aged at 1200°F for 1000 hours
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-120® alloy, solution heat-treated aged at 1400°F for 1000 hours
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-120® alloy, solution heat-treated aged at 1600°F for 1000 hours
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-120® alloy, solution heat-treated aged at 1800°F for 1000 hours
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy plate, aged 1000 hours at 649°C (1200°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy plate, aged 4000 hours at 649°C (1200°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy, annealed plate
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy, hot rolled and solution annealed plate
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy, plate, aged 4000 hours at 760°C (1400°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy, plate, aged 4000 hours at 871°C (1600°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy, plate, aged 8000 hours at 760°C (1400°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy, plate, aged 8000 hours at 871°C (1600°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy, solution annealed sheet
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-120® alloy, solution heat-treated plate
Excellent strength at elevated temperatures, combined with good resistance to carburizing and sulfidizing environments. Applications include bar frame heat treating baskets, wire mesh furnace belts ..
Electrical Resistivity 0.0001231 ohm-cm

@Temperature 700 °C
0.0001231 ohm-cm

@Temperature 1290 °F
Haynes HR-160® alloy plate, aged 8000 hours at 649°C (1200°F)
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Copyright © lookpolymers.com All Rights Reserved