Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | 5 mm/min |
Polimeri Europa EDISTIR N1460 Polystyrene
(discontinued **) Symbol according to ISO 1043-1: PS Designation: Thermoplastic ISO 1622-PS,E,085-03 High molecular weight general purpose polystyrene with good mechanical strength. This grade is especially recomme.. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Kleerdex Kydex® 130 Acrylic/PVC Thermoplastic Sheet
(discontinued **) Decorative thermoplastic sheetApplications: Appliances, laminations, electronics, in-store displays, medical devices, equipment housings, dental equipmentFeatures: For deep to hard to form parts or .. |
|||
Tensile Strength, Ultimate | 41.0 - 107 MPa | 5950 - 15500 psi | Average value: 77.7 MPa Grade Count:13 |
Overview of materials for Epoxy, Encapsulating, Glass or Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Encapsulating, Glass or Mineral Filled". Each property range of values reported is minimum and ma.. |
|||
Tensile Strength, Ultimate | 41.0 - 62.0 MPa | 5950 - 8990 psi | Average value: 53.6 MPa Grade Count:10 |
Overview of materials for Phenolic, Novolac, Mineral/Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Fiber Filled". Each property range of values reported is minimum and maximum .. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Plenco 506 Black Heat Resistant Mineral Filled Phenolic Molding Compound
(discontinued **) Plaslok 506 is a two-stage, mineral-filled phenolic molding compound. It is formulated for automotive ashtrays and for appliance applications such as utensil handles receiving repeated exposure to .. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Plaslok 506 Black Heat Resistant Mineral Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 506 is a two-stage, mineral-filled ph.. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
IDI Composites 44-10 Thermoset Polyester, Molding Multi-purpose medium strength material with excellent surface appearance, corrosion resistance, and V-O flame resistance.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | |
Haysite 14100 Polyester BMC, 15% Glass Reinforced The 14100 series bulk molding compound is an electrical grade material that can be compression, transfer, or injection molded. Offering good mechanical strength and excellent electrical properties, .. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | |
Haysite 14200 Polyester BMC, 15% Glass Reinforced The 14200 series bulk molding compound is one of Haysite's newest molding compound families. This grade can be compression, transfer, or injection molded. Good mechanical strength and exceptional a.. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
KYDEX® 6200 Thermoplastic Sheet Fire rated sheet for mass transitApplications: Dashboards, seatbacks, armrests, tray tables, window reveals, cabin linersFeatures: Kydex 6200 is a proprietary, high performance thermoplastic sheet. .. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Sumitomo Bakelite North America 4064 Mineral Filled Electrical Encapsulation Grade Epoxy Rogers electrical encapsulation grade epoxy is recommended for capacitors, resistors, gold lead encapsulation, relays, coils and bobbins.Information provided by Sumitomo Bak North America, Inc. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Sumitomo Bakelite North America RX® 431 Cellulose Reinforced Phenolic Novolac RX431 is a cellulose fiber reinforced phenolic novolac molding compound. This material is recommended for large parts requiring moderate toughness. It is designed to meet the requirements of ASTM D.. |
|||
Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
Cosmic Plastics 6220F Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
Cosmic Plastics K31 Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
Cosmic Plastics K61 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
Cosmic Plastics K66 Long Glass Fiber Filled Iso Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Plenco 6343 Phenolic, Granular, Transfer Molded PLENCO 06343 is a mica reinforced phenolic molding compound, offering for a low power factor, low electrical losses, and good electrical properties after long exposures to high humidity. UL recogniz.. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Plenco 7203 Phenolic, Granular, Transfer Molded PLENCO 07203 is an organic fiber reinforced phenolic molding compound, offering improved mechanical strength and an industrial finish. UL recognized under component file E40654. 07203 is available i.. |
|||
Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
Cosmic Plastics D69 Long Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
Cosmic Plastics D72 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ISO 527-1, 2 |
Polyplastics Duracon® TD-15 Acetal Co-polymer (POM), High impact, Flexible DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O).. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ISO 527 |
DSM Fibre Intermediates Nyrim® 2025 (Wollastocoat®), Dry Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is processed via Reaction Injection Moulding (RIM) tec.. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ATSM D638 |
Ashley Polymers Ashlene® 527LDMS Nylon 66 A very high impact Nylon 66 with Molybdenum disulfide designed to combine high impact with a reduced co-efficient of friction.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ATSM D638 |
Ashley Polymers Ashlene® 940H Nylon 11 A general purpose highly flexible natural Nylon 11 resin with UV stabilizers.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Kleerdex Kydex® 1900 Acrylic/PVC Thermoplastic Sheet
(discontinued **) Mid-temperature aircraft gradeApplications: This sheet product is designed for use in small aircraft interiors but also is appropriate for other applications where higher in-service temperatures may.. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Plenco 301 Black Impact Grade Woodflour/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok 301 is a two-stage, woodflour and flock-filled phenolic molding compound. It has broad molding latitude combined with good electrical properties and improved impact strength. It is particu.. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Plenco 302 Black Impact Grade Woodflour/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok 302 is a two-stage, woodflour and flock-filled phenolic molding compound. It has low specific gravity, broad molding latitude and an excellent balance of electrical and physical properties... |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Plaslok 302 Black Impact Grade Woodflour/Flock Filled Phenolic Molding Compound
(discontinued **) Plaslok Corporation was purchased by Plastics Engineering Company (maker of Plenco brand materials) in March 2000. The Plaslok name is no longer in use.Plaslok 302 is a two-stage, woodflour and flo.. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
Sumitomo Bakelite North America FM 7700P Fiberglass and Mineral Reinforced Phenolic Novolac FM 7700P is a two-stage phenolic molding compound reinforced with cotton fabric in pellet form. FM-7700P is recommended to customers desiring approval under ASTM D-5948-96,Type CFI-20. (Replaces Mil.. |
|||
Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | |
Cosmic Plastics D44 Mineral Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |